Abstract:In this work, the effect of single roll drive cross rolling on the microstructure, crystallographic texture, hardness, tensile properties, and fracture behavior of AA7075 aluminum alloy was investigated. It was found that with increasing the thickness reduction, the grain size reduced and the average width of grain for the 40% deformed sample decreased to 3.7 ± 0.4 µm. Due to the nature of the cross-rolling process, several X-type shear bands were observed after 40% deformation. The recrystallization texture is notably intensified to its highest value of 4.4 × R, after only 20% cold deformation due to the occurrence of continuous dynamic recrystallization (CDRX). The intensity of recrystallization texture sharply dropped to its lowest value of 2.7 × R. This was due to the rotation of Goss-orientated new grains in the 20% deformed sample toward copper orientation during 40% rolling. With increasing the thickness reduction, the overall texture intensity significantly reduced owing to the nature of the cross-rolling process in which the rolling direction rotates 90° after each 10% strain. Two texture transitions were observed along τ fiber: rolling (copper) texture to recrystallization (Goss) texture after 20% thickness reduction and recrystallization to the rolling texture after 40% deformation. The hardness and strength increased by increasing the thickness reduction, while the ductility decreased. After a 40% thickness reduction, yield strength significantly increased from 138.3 ± 4.4 MPa (for initial sample) to the highest value of 580.5 ± 11.5 MPa, demonstrating 320% increment, in the 0° direction. This increment for 45° and 90° direction was 265% and 337%, respectively. By 40% rolling, the value of in-plane anisotropy (IPA) remarkably decreased to its lowest value of 3.4% due to texture weakening. With increasing the rolling reduction to 20%, the severity of Portevin–Le Chatelier (PLC) increased in the flow curves due to the occurrence of CDRX and also strengthening of the rotated cube {001} < 110 > and E {111} < 110 > components. With increasing the rolling reduction, the size of cleavage facets and the severity of delamination increased, and the number and depth of dimples decreased.

Study on Rolling Defects of Al-Mg Alloys with High Mg Content in Normal Rolling and Cross-Rolling Processes

Study on Forming Defects in the Rolling Process of Large Aluminum Alloy Ring Via Adaptive Controlled Simulation

Unveiling the Underlying Mechanism of Forming Edge Cracks Upon High Strain-Rate Rolling of Magnesium Alloy

The Effect of Texture on the Very High Cycle Fatigue Performance and Deformation Mechanism of Rolled AZ31B Magnesium Alloys

Effect of rolling geometry on the mechanical properties, microstructure and recrystallization texture of Al-Mg-Si alloys

A continuum damage model for Mg/Al composite sheets rolling: Theoretical development and application

Effect of single roll drive cross rolling on the microstructure, crystallographic texture, and mechanical behavior of Al–Zn–Mg–Cu alloy

Microstructural analysis of edge cracking in magnesium alloy sheet under rolling

Crystal Plasticity Finite Element Simulation of Grain Evolution Behavior in Aluminum Alloy Rolling

Comparison of edge crack behavior of Mg sheets prepared by online heating rolling

Effect of variable thickness cross rolling on edge crack and microstructure gradient of AZ31 magnesium alloy

Effect of Rolling on Crack Behavior of FeCrAl Alloys in Ultra-Long Life

Initiation and Suppression of Crack Propagation during Magnesium Alloy Rolling

Effect of rolling deformation and passes on microstructure and mechanical properties of 7075 aluminum alloy

Prediction of edge cracks and plastic-damage analysis of Mg alloy sheet in rolling

The Edge Crack, Texture Evolution, and Mechanical Properties of Mg-1Al-1Sn-Mn Alloy Sheets Prepared Using On-Line Heating Rolling

Effect of Large Strain Cross Rolling on Microstructure and Properties of Al−Li Alloy Plates with High Magnesium Content

The Role of Al Content on Deformation Behavior and Related Texture Evolution During Hot Rolling of Mg-Al-Zn Alloys

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Influence of Asymmetric Rolling on the Microstructure, Texture Evolution and Mechanical Properties of Al–Mg–Si Alloy

Effect of Rolling Strain on Microstructure and Tensile Properties of Dual-Phase Mg–8Li–3Al–2Zn–0.5Y Alloy