Abstract:This study investigated defect formation and strain distribution in high-Mg-content Al-Mg alloys during normal rolling and cross-rolling processes. The finite element analysis (FEA) revealed the presence of wave defects and strain localization-induced zipper cracks in normal cold rolling, which were confirmed by the experimental results. The concentration of shear strain played a significant role in crack formation and propagation. However, the influence of wave defects was minimal in the cross-rolling process, which exhibited a relatively uniform strain distribution. Nonetheless, strain concentration at the edge and center regions led to the formation of zipper cracks and edge cracks, with more pronounced propagation observed in the experiments compared to FEA predictions. Furthermore, texture evolution was found to be a crucial factor affecting crack propagation, particularly with the development of the Goss texture component, which was observed via electron backscattered diffraction analysis at bending points. The Goss texture hindered crack propagation, while the Brass texture allowed cracks to pass through. This phenomenon was consistent with both FEA and experimental observations. To mitigate edge crack formation and propagation, potential strategies involve promoting the formation of the Goss texture at the edge through alloy and process conditions, as well as implementing intermediate annealing to alleviate stress accumulation. These measures can enhance the overall quality and reliability of Al-Mg alloys during cross-rolling processes. In summary, understanding the mechanisms of defect formation and strain distribution in Al-Mg alloys during rolling processes is crucial for optimizing their mechanical properties. The findings of this study provide insights into the challenges associated with wave defects, strain localization, and crack propagation. Future research and optimization efforts should focus on implementing strategies to minimize defects and improve the overall quality of Al-Mg alloys in industrial applications.

Edge crack forming mechanism and the countermeasures in as‐sintered 2024 aluminium alloy during cold rolling

Reason for Edge Cracking of Cold-Rolled 55Mn Strip Steel and the Cold-rolling Control Measures

Unveiling the Underlying Mechanism of Forming Edge Cracks Upon High Strain-Rate Rolling of Magnesium Alloy

Micro Crack of Aluminum Sheet During Cold Rolling

The Causes and Control of Longitudinal Edge Cracks of the Plate

Comparison of edge crack behavior of Mg sheets prepared by online heating rolling

Initiation and Suppression of Crack Propagation during Magnesium Alloy Rolling

Study on the formation of alligator crack and edge crack in high silicon grain oriented electrical steel during cold rolling

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Numerical Analysis of Edge Cracking in High-Silicon Steel during Cold Rolling with 3D Fracture Locus

Effect of rolling reduction rate on the forming of microstructures on the surface of 2024 aluminum alloy

Steel Edge Cracking Analysis and Improvement Measures

Edge-crack free and high mechanical properties of AA7075 sheets by using cryorolling and subsequent aging

Ameliorating the edge cracking behavior of Mg-Mn-Al alloy sheets prepared by multi-pass online heating rolling

Inhibition Behavior of Edge Cracking in the AZ31B Magnesium Alloy Cold Rolling Process with Pulsed Electric Current

Study on Rolling Defects of Al-Mg Alloys with High Mg Content in Normal Rolling and Cross-Rolling Processes

Predicting of Edge Crack Behavior of Steel Sheet in the Cold Rolling Process Based on Cohesive Zone Model

Application of the Cohesive Zone Model for Analysing the Edge Crack Propagation of Steel Sheet in the Cold Rolling Process

Influence of Deformation on Precipitation Behavior of 2024al Alloy

Effects of Cold Rolling Pre-Strain on Abnormal Grain Growth Behavior in Longitudinal Welds of 2196 Al-Cu-Li Profiles

Uncommon Cold-Rolling Faults in an Fe–Mn–Si–Cr Shape-Memory Alloy