Abstract:It is fundamentally important to understand the influence of strain on the density of deformation twins in TWIP steel because twinning is its dominant deformation mechanism.The deformation behavior of a Fe -30Mn - 4Si-3Al-0.097C steel has been investigated by X -ray diffraction(XRD),electron backscatter diffraction (EBSD) and transmission electron microscopy(TEM) techniques.Sample with an average grain size of 10μm was deformed in cold - rolling with a reduction of 10%,20%,30%,40%,50%,60%and 70%,respectively. The mechanical properties of the cold - rolled samples were further investigated by tensile tests.The yield strength (σy) and ultimate - tensile - strength(σUTS) of the as - prepared sample is 480 MPa and 850 MPa, respectively.However,under cold rolling deformation,the tensile strength obviously increases with an increase in rolling reduction.The sample with a rolling reduction of 10%exhibitsσy of 610 MPa andσUTS of - 1000 MPa. The yield strength and tensile strength are further enhanced up to 1320 MPa and 1 378 MPa for the specimen with a rolling reduction of 70%,regardless of the poor ductility of 6.7%.The deformation microstructures were studied by EBSD and TEM observations.It is found that,with increasing rolling reduction,the average distance between deformation twins decreases gradually while the density of deformation twins(the length of twin boundary in unit area) exhibit a maximum value at 40%cold-rolling + tension.Carefully statistics analysis reveals grain orientation is closely related to the deformation twins and the underlying mechanism governing the twinning is discussed.

Cracking in a Fe–25Mn–3Si–3Al Steel

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

In-situ Observation of Crack Evolution in Ti/Al Laminated Composite

Study of Q345 Steel under Tensile Failure with Bilateral Parallelcracks

The study of the tensile fracture process of Al-Li alloys

Tensile Fracture Modes in Fe-22Mn-0.6C and Fe-30Mn-3Si-3Al Twinning-Induced Plasticity (TWIP) Steels

Deformation Twinning in Response to Cracking in Al: an in Situ TEM and Molecular Dynamics Study

In-situ SEM study of fracture mechanism in fully lamellar Ti-49at% Al Alloy

A Study of Crack and Fracture on the Welding Joint of Fe3Al and Cr18–Ni8 Stainless Steel

In-situ TEM Investigation of Fracture Process in an Al–Cu–Mg Alloy

Tensile deformation and fracture of Ti-5Al-5V-5Mo-3Cr-1.5Zr-0.5Fe alloy at room temperature

Microstructures and Deformation Mechanisms of Cr26Mn20Fe20Co20Ni14 Alloys

Initial Microstructure Effects on Hot Tensile Deformation and Fracture Mechanisms of Ti-5Al-5Mo-5V-1Cr-1Fe Alloy Using in Situ Observation

Investigation On In-Situ Tensile Of Extruded 1420 Al-Li Alloy

Deformation and Recrystallization Behavior of a Fe-30Mn-4Si-3Al-0.097C Steel

Deformation Mechanisms of a 20mn TWIP Steel Investigated by in Situ Neutron Diffraction and TEM

In Situ SEM Investigation of Tensile Fracture Process of Fe-25Cr-35Ni Based Superalloy

Strain rate-dependent hardening with dislocation-twin interaction of Fe–Mn–Al–C steel using crystal plasticity

Interaction of Crack with Twins in Hot-Rolling Az31 Magnesium Alloys During In-Situ Tem Straining Experiments

A Study of Crack Initiation in a Low Alloy Steel

In Situ Observation of the Tensile Deformation and Fracture Behavior of Ti–5Al–5Mo–5V–1Cr–1Fe Alloy with Different Microstructures