Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Quasi-in-situ observations of crack propagation and microstructure evolution of high manganese austenitic steel at −196 °C

Fracture Behaviour of 8ni 980 MPa High Strength Steel at Various Temperatures Part 2 – COD Tests

Cracking in a Fe–25Mn–3Si–3Al Steel

Crack propagation behavior of dual-phase steel at low temperature

In-Situ Study of High Temperature Tensile Fracture Mechanism of Mar-M247 Alloy

Molecular dynamics simulation-based representation of intergranular fracture processes in austenitic steel

Interpretation of Significant Decrease in Cryogenic-Temperature Charpy Impact Toughness in a High Manganese Steel

Low-Temperature Deformation and Fracture of Cr-Mn-N Stainless Steel: Tensile and Impact Bending Tests

Further investigation of critical events in cleavage fracture of C-Mn base and weld steel

Interpretation of microstructure evolution and mechanical properties under aging treatments of a Fe–24Mn-0.6C–2Al-0.6V austenitic steel for cryogenic application

Temperature dependence of the deformation behavior and mechanical properties of a Fe–Mn–Al–C low-density steel for cryogenic application

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Grain Size Dependence of Twinning Behaviors and Resultant Cryogenic Impact Toughness in High Manganese Austenitic Steel

In-Situ Synchrotron X-Ray Diffraction Study on Stress-Induced Martensite Transformation in Maraging Steel with High Strength and Good Ductility

Temperature Dependence of Deformation Behaviors in High Manganese Austenitic Steel for Cryogenic Applications

Simultaneous Enhancement of Strength and Ductility in a Finegrained Fe-30Mn-0.11C Steel at 77 K

In-Situ Sem Observation on Fracture Behavior of Austempered Silicon Alloyed Steel

Tailoring the Microstructure to Enhance the Cryogenic Mechanical Properties of a Fe–34.5mn–0.04c Steel

Evolution of Microstructures and Mechanical Properties During Solution Treatment of a Ti–V–Mo-containing High‑manganese Cryogenic Steel

Deformation microstructures as well as strengthening and toughening mechanisms of low-density high Mn steels for cryogenic applications

Superior fracture toughness in a high-strength austenitic steel with heterogeneous lamellar microstructure