Abstract:Abstract Central cracking in cross-wedge-rolled workpieces results in high wastage and economic loss. Recent cross-wedge rolling tests on two batches of steel showed that one batch formed central cracks, while the other was crack-free. The batches were both nominally of the same chemical composition and thermomechanical treatment history. In addition, both batches had passed all the standard quality assessments set for conventional forging processes. It was suspected that the different cracking behaviours were due to differences in microstructure between the two as-received steel billets, and the material in cross-wedge rolling (CWR) was more sensitive to the initial microstructure compared with other forging processes due to its specific loading condition including ostensibly compression and large plastic strain. Nevertheless, no previous study of this important problem could be identified. The aim of this study is, therefore, to identify the key microstructural features determining the central crack formation behaviour in CWR. The hot workability of the as-received billets was studied under uniaxial tensile conditions using a Gleeble 3800 test machine. Scanning electron microscope with energy-dispersive X-ray spectroscopy and electron backscatter diffraction was applied to characterise, quantitatively analyse, and compare the chemical composition, phase, grain, and inclusions in these two billets, both at room temperature and also at the CWR temperature (1080 °C). Non-metallic inclusions (oxides, sulphides, and silicates) in the billets were determined to be the main cause of the reported central cracking problem. The ductility of the steels at both room and elevated temperatures deteriorated markedly in the presence of the large volumes of inclusions. Grain boundary embrittlement occurred at the CWR temperature due to the aggregation of inclusions along the grain boundaries. It is suggested that a standard on specifying the inclusion quantity and size in CWR billets be established to produce crack-free products.

The Causes and Control of Longitudinal Edge Cracks of the Plate

Study on Measurement Method of Interior Stress Distributions in Engineering Rolled-Plates

Reason for Edge Cracking of Cold-Rolled 55Mn Strip Steel and the Cold-rolling Control Measures

The Cracks on Slab Corner During Hot Rolling Process

Crack mechanism and experimental verification on straightening of AZ31B magnesium alloy plate

Formation mechanism and control strategy of M-shaped and W-shaped profile defects in hot rolling of aluminum plate

Study on Surface Longitudinal Crack Formation of Typical Hypoeutectoid Steel Produced on a Caster with Billet and Slab

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

Effect of Rolling Process Parameters on Transverse Cracks on the Surface of Q345 Steel

Effects of Heat Treatment Process on Microstructure and Mechanical Properties for Extra-Thick High-Strength Steel Plate

Fracture failure analysis and research on super-large-diameter roll

Analysis and control of surface cracks in a B-bearing continuous casting blooms

Numerical and experimental analysis of edge wave defect control during TA2 circular tube cold roll forming

Cause Analysis and Preventive Measures against Cracks in 15Cr1Mo1V Steel Welded Joint in Service

Research on the Temperature and Thermal Stress of the Roll Quenching Process of Thin Plates

A Method to Control the Transverse Corner Cracks on a Continuous Casting Slab by Combining Microstructure Analysis with Numerical Simulation of the Slab Temperature Field

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Numerical Analysis on Flatness Adjusting Performance of Hot Wide Strip Temper Mill with Small-Diameter Work Rolls

Analysis of Edge Crack Defect Analysis and Control of 316L Austenitic Stainless Steel

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

Analysis of Internal Cracks in Continuous Casting Slabs with Soft Reduction