Abstract:The casting-rolling compound forming process of ring parts is an advanced plastic forming technology that has been developed due to the merits of high efficiency and energy and material saving. However, cracks often occur during the hot ring rolling process, especially at the edges of the ring parts, which severely affects the forming quality. To predict and try to avoid the occurrence of cracks in the casting-rolling compound forming process of ring parts, the high-temperature fracture behaviors of as-cast 42CrMo steel were investigated by thermodynamic experiment method. The high-temperature tensile tests were carried out using the Gleeble-3500D thermomechanical simulator at various temperatures and strain rates. Stress-strain curves and fracture morphology were examined, through which the sensitivity of stress to temperature and strain rate and the effect of dynamic recrystallization and cavity evolution on fracture were found. The law of critical fracture strains was analyzed, and the model of critical fracture strain as a function of temperature and strain rate was established. Based on Oyane criterion, the thermal ductile fracture criterion was established in conjunction with the model of critical fracture strain. By embedding this thermal damage model into the finite element (FE) model for hot ring rolling of an as-cast 42CrMo ring, the damage prediction for this process was realized, and the thermal ductile fracture criterion was proved to be reliable. From the FE results for hot ring rolling, mechanism of damage and fracture in the hot ring rolling process was analyzed. The damage threshold C f is small, and the damage ratio D is large at the top and bottom edges of the inner surface area of the ring, which have the greatest propensity to cracking in the course of hot ring rolling. This is of great significance in terms of improving the forming quality of ring parts in the casting-rolling compound forming process.

Fracture failure analysis and research on super-large-diameter roll

Fracture failure analysis on Alloy783 bolts in medium-pressure valve bonnets of USC units

Fracture Analysis of High Chromium Cast Iron Roll on CSP Mill

Fracture failure analysis of 21CrMoV5.11 steel continuous casting roller

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

The Causes and Control of Longitudinal Edge Cracks of the Plate

Influence of Work Hardening on the Surface of Backup Rolls for a 4-High Rolling Mill Fractured during Rolling Campaign

Analysis of the Influence of Contact Stress on the Fatigue of AD180 High-Carbon Semi-Steel Roll

Material Analysis of the Fatigue Mechanism of Rollers in Tapered Roller Bearings

Failure Analysis of Fatigue Fracture on the Outer Ring of a Cylindrical Roller Bearing in an Air Blower Motor

Study on High Chromium Cast Iron Fracture Grinding Roll

Investigation and prediction of central cracking in cross wedge rolling

Failure Analysis of a Working Roll under the Influence of the Stress Field Due to Hot Rolling Process

Subsurface propagation of partial ring cracks under rolling contactPart II. Fracture mechanics analysis

Failure analysis for outer ring cracking of GCr15 rolling bearing

Fracture Failure Analysis of Twin Rolling Casting Magnesium by Hot Compression

Failure Analysis on Fracture of 16mn Steel

Fracture failure analysis of vertical arm of rear axle

Establishment of Thermal Ductile Fracture Criterion for As-Cast 42CrMo Steel and Its Application in Hot Ring Rolling Process

Research on the failure mechanism of the high-speed train bearing steel under static load failure

Fracture failure analysis of the main shaft of a large sewage treatment equipment