Effects of 1 MeV Electron Irradiation on Β-Ga2o3 Photodetectors
Tianqi Wang,Shenghuan Wang,Bin Zhou,Yun Tang,Lei Wang,Bo Li,Chaoming Liu,Zhenping Wu,Yongtao Yang,Bo Mei,Chunhua Qi,Yanqing Zhang,Ming Liu
DOI: https://doi.org/10.1149/2162-8777/ac2e4d
IF: 2.2
2021-01-01
ECS Journal of Solid State Science and Technology
Abstract:In this paper, the electrical and ultraviolet optoelectronic properties of the interdigitated finger geometry beta-Ga2O3 photodetector were investigated before and after 1 MeV electron irradiation. Under the dark condition, the voltage at which the minimum current was located shifted from 0 V to -9.5 V after the electron irradiation. As the fluence increased from 5.0 x 10(13) cm(-2) to 1.0 x 10(15) cm(-2), the current at the voltage of 3 V of the beta-Ga2O3 photodetector increased from 0.047 nA to 0.121 nA. The negative deviation of the minimum current was related to the positive charge trap caused by electron irradiation, while the improvement of the current was related to the fact that the electron irradiation produced a large number of electron-hole pairs. Under 365-nm illumination, the current at the voltage of 3 V of the beta-Ga2O3 photodetector increased from 0.199 nA to 0.898 nA, as the fluence increased from 5.0 x 10(13) cm(-2) to 5.0 x 10(14) cm(-2); then, it dropped to 0.779 nA when the fluence reached 1.0 x 10(15) cm(-2). The increase of the current was due to the increase of defects generated by the electron irradiation under 365-nm illumination. Also, the decline of the current at the fluence of 1.0 x 10(15) cm(-2) may be caused by the quenching effect. Under 254-nm illumination, the current at the voltage of 3 V of the beta-Ga2O3 photodetector dropped from 78.566 nA to 19.362 nA after the electron irradiation. This change was due to the lattice distortion and the reduction of the defect energy. However, as the fluence of the irradiation increased, the current increased gradually. This may be related to the increase of defects excited by electrons.(C) 2021 The Electrochemical Society ("ECS"). Published on behalf of ECS by IOP Publishing Limited.