Abstract:Barium titanate powder with average particle size near 300 nm was produced using the low-temperature synthesis. It was established using scanning electron microscopy that at the thermal treatment, the particles gradually decrease with the formation of polydisperse aggregates. Based on the thermogravimetric analysis of the synthesized powder held in air for 4 months, it was shown that along with the low-temperature phase, the sample contains a high-temperature phase of carbonates, which removes at ~ 900 °C. Sorption characteristics of barium titanate thermally treated at various temperatures were obtained from the results of adsorption-desorption of nitrogen vapors. The specific surface area of the BaTiO3 powder was 76 m2/g. It was found that further heat treatment leads to a decrease in the specific surface area. The X-ray diffraction analysis of barium hydroxotitanil annealed at temperatures from 120 °C to 800 °C showed that the thermal treatment of the sample leads to the formation of a completely formed phase of barium titanate. The DSC temperature was used to determine the Curie temperatures for a HTB powder thermally treated in the temperature range from 120 to 800 °C. Dielectric spectra of suspensions of the synthesized powder were obtained during the heat treatment. . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . . .

Low-temperature Preparation of Pure BaTiO_(3) by SAG Method

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

A simple approach to porous low-temperature-sintering BaTiO 3

Synthesis of BaTio3 nanocrystals by stearic acid gel method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Low-temperature combustion synthesis of nanometer tetragonal barium titanate powders

Preparation of Nanoscaled BaTiO3 Powders by DSS Method Near Room Temperature under Normal Pressure

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Low-temperature Combustion Synthesis and Characterization of Nanosized Tetragonal Barium Titanate Powders

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

The Synthesis of Ultrafine Ba/Sr Titanate Powders

Process for Non-Agglomerated Nanometer-Sized Barium Titanate Powders by Sol-Gel Auto-Igniting Synthesis

LOW-TEMPERATURE SYNTHESIS OF BARIUM TITANITE IN AQUEOUS SOLUTION