A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion
Dongdong Zhang,Qiang Yang,Kai Guan,Baishun Li,Nan Wang,Pengfei Qin,Bo Jiang,Chi Sun,Xin Qin,Zheng Tian,Zhanyi Cao,Jian Meng
DOI: https://doi.org/10.1016/j.jallcom.2019.151967
IF: 6.2
2019-11-01
Journal of Alloys and Compounds
Abstract:<p>A high-strength low-rare-earth-alloyed Mg−3.5Sm−2Yb−0.6Zn−0.4Zr alloy was processed by an ingot metallurgy process with hot-extrusion followed by artificial aging. The peak-aged sample exhibited a higher yield strength of 449 MPa than most of extruded Mg−Gd based alloy containing high RE content, and even is comparable to that of the T8-treated 2024 Al alloy. The studied alloy exhibited a typical bimodal microstructure, consisting of dynamically recrystallized (DRXed) grains with random textures and coarse unrecrystallized regions with strong basal fiber texture. In addition, the fragmented Mg<sub>5</sub>RE and Mg<sub>41</sub>RE<sub>5</sub> phases distributed at extrusion stringers. Abundant of fine Mg<sub>3</sub>RE particles precipitated dynamically in DXRed regions, which restrains DRXed grains growth effectively by grain boundary pinning. Within the unDXRed regions, uniformly dense Mg<sub>3</sub>RE and Mg<sub>12</sub>RE nano-precipitates were observed. Also there were many basal <<strong>a</strong>> dislocations and a few non-basal <<strong>c</strong> + <strong>a</strong>> dislocations in unDXRed regions. Subsequent artificial ageing significantly enhanced the alloy's strength by introducing basal precipitates, although decreased the ductility slightly. Finally, the ultrahigh yield strength was revealed to be attributed to the combined effects of a strong basal fiber texture, a bimodal microstructure, and numerous precipitated particles.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering