Creep behavior and dynamic precipitation of highly heat-resistant Mg alloy with low rare-earth content

Yaqin Zhang,Yan Hong,Hangyu Li,Deping Zhang

DOI: https://doi.org/10.1016/j.jallcom.2024.174960

IF: 6.2

2024-05-26

Journal of Alloys and Compounds

Abstract:Achieving high creep resistance in low rare-earth (RE) containing Mg alloys is quite difficult due to the limited precipitation density. Here we reported a low-RE-alloyed Mg alloy (RE = 4 wt %) with good creep resistance, which is superior to most heat-resistant Mg benchmark alloys. Our creep-resistant alloy is characterized by nano-spaced stacking faults (SFs) in grain interiors and thermally stable Mg 2 RE phases at grain boundaries. Both intragranular SFs and grain-boundary Mg 2 RE phase remain the unharmed structures, with no obvious decomposition or coarsening after the creep at 200 and 220 oC for 100 h. During creep, a large amount of dynamic precipitation such as discrete β particles and basal γ'' phases was introduced, which plays a crucial role in resisting the creep deformation within grains. As a result, nano-spaced SFs, thermally stable Mg 2 RE skeletons at grain boundaries, and dynamic precipitation of β and γ'' phases are responsible for the enhanced creep resistance of this alloy. After creep, the alloy exhibits abnormally high stress exponents ( n = 9.2 at 200oC and n = 9.3 at 200oC) and stress-dependent activation energies of 105–153 kJ/mol at 90–120 MPa. High stress exponents can be normalized to be 3–4 using the threshold stress approach or Garofalo's sinh relation, suggesting that dislocation climb acts as the operative creep mechanism. Finally, we proposed a strategy to develop highly creep-resistant low-RE-alloyed Mg alloys via constructing thermally stable microstructures at grain boundaries and interiors.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering