Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

The Development of a High-Strength Mg-10.3Gd-4.4Y-0.9Zn-0.7Mn Alloy Subjected to Large Differential-Thermal Extrusion and Isothermal Aging

Mechanism of high-strength and ductility of Mg-RE alloy fabricated by low-temperature extrusion and aging treatment

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Development and characteristics of a low rare-earth containing magnesium alloy with high strength-ductility synergy

Fabrication of magnesium alloy with high strength and heat-resistance by hot extrusion and ageing

Achieving ultrahigh strength in pre-ageing-extruded Mg-Gd-Y-Zn-Mn alloys via ageing treatment

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

Improving Strength and Ductility of Mg–Gd–Y–Zn–Zr Alloy Simultaneously Via Extrusion, Hot Rolling and Ageing

Preparation of high-performance Mg-Gd-Y-Mn-Sc alloy by heat treatment and extrusion

Revealing precipitation behavior and mechanical response of wire-arc directed energy deposited Mg-Gd-Y-Zr alloy by tailoring aging procedures

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Strengthening of Mg Alloy with Multiple RE Elements with Ag and Zn Doping via Heat Treatment

Preparation of ultra-high strength Mg-Gd-Y-Zn-Zr alloy by pre-ageing treatment prior to extrusion

Fine-grained Mg–1Mn–0.5Al–0.5Ca–0.5Zn alloy with high strength and good ductility fabricated by conventional extrusion

Excellent isotropic mechanical properties of directed energy deposited Mg-Gd-Y-Zr alloys via establishing homogeneous equiaxed grains embedded with dispersed nano-precipitation

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

Achieving Ultra-High Strength in Mg–Gd–Ag–Zr Wrought Alloy Via Bimodal-Grained Structure and Enhanced Precipitation