Abstract:Mg-0.7Al-0.3Ca-0.4Mn (AXM070304, wt.%) alloy was subjected to extrusion with a ram speed of 1 mm/s and an extrusion ratio of 25:1. The extrusion temperature varies from 170 °C to 400 °C. The influence of extrusion temperature on microstructure and mechanical properties of the dilute AXM070304 alloy was systematically explored. With raising the extrusion temperature, the average size of the dynamic recrystallized (DRXed) grains was increased, while the intensity of the basal fiber texture was decreased. When the extrusion temperature was escalated from 170 °C to 400 °C, the tensile yield strength (YS) of the low-alloy AXM070304 extrusion alloy was decreased from 437 to 246 MPa, while the elongation to failure (EL) was increased from 2.9 to 16.9%. The alloy extruded at 200 °C obtains an YS of 412 MPa, an ultimate tensile strength (UTS) of 418 MPa and an EL of 14.8%, exhibiting excellent ductility and ultrahigh strength. The ultrahigh YS was mainly due to the strengthening from ultra-fine recrystallized grains (0.61 μm) with grain boundary segregation of solute Al and Ca atoms. The growth of DRXed grains was inhibited mainly by the co-segregation of Al atoms and Ca atoms, nanosized Al 2 Ca and β-Mn particle phases at the grain boundaries. Plastic instability occurred under tensile loading in the ultrafine-grained AXM070304 alloy, which may be due to the fact that the grain boundary segregation of Al atoms and Ca atoms requires a high energy barrier for dislocation emission. Once the tensile stress reaches the peak value, the mobile dislocation density increases suddenly.

Fine-grained Mg–1Mn–0.5Al–0.5Ca–0.5Zn alloy with high strength and good ductility fabricated by conventional extrusion

Microstructure modification and precipitation strengthening for Mg–6Zn–1Mn–4Sn–0.5Ca through extrusion and aging treatment

Microstructure, Tensile Properties and Work Hardening Behavior of an Extruded Mg–Zn–Ca–Mn Magnesium Alloy

Low-cost and high-strength Mg-Al-Ca-Zn-Mn wrought alloy with balanced ductility

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion

Fabrication of magnesium alloy with high strength and heat-resistance by hot extrusion and ageing

Microstructure and Mechanical Property of Mg-13Gd-0.2Ni Alloy Processed by Extrusion and Aging

Preparation of high-performance Mg-Gd-Y-Mn-Sc alloy by heat treatment and extrusion

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Ultrafine-grained Al–Zn–Mg–Cu alloy processed via cross accumulative extrusion bonding and subsequent aging: Microstructure and mechanical properties

Effect of Zn Concentration on the Microstructures and Mechanical Properties of Extruded Mg–7Y–4Gd–0.4Zr Alloys

Tailoring strength and ductility of Mg97Y2Zn1 alloy through the architecture of heterogeneous lamellar structure by large-ratio hot extrusion

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Development of ultrahigh-strength low-alloy Mg-0.7Al-0.3Ca-0.4Mn (wt.%) alloy with excellent ductility via controlling extrusion temperature

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting

Achieving ultrahigh strength in pre-ageing-extruded Mg-Gd-Y-Zn-Mn alloys via ageing treatment

Microstructural evolution and mechanical properties of an ultrahigh-strength Al−Zn−Mg−Cu alloy via powder metallurgy and hot extrusion

Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment