Abstract:n ultra-strong and ductile Mg-8.2Gd-3.8Y-1Zn-0.4Zr (wt pct) alloy was developed by using hot extrusion to modify the microstructure via forced-air cooling and an artificial aging treatment. A superior strength–ductility balance was obtained that had a tensile yield strength of 466 MPa and an elongation to failure of 14.5 pct. The local strain evolution during the in situ testing of the ultra-strong and ductile alloy was quantitatively analyzed with high-resolution electron backscattered diffraction and digital image correlation. The fracture behavior during the tensile test was characterized by synchrotron X-ray tomography along with SEM and STEM observations. The alloy showed a bimodal microstructure, consisting of dynamically recrystallized (DRXed) grains with random orientations and elongated hot-worked grains with ⟨ 101̅0⟩ parallel to the extrusion direction. The DRXed grains were deformed by the basal 〈a〉 slip and the hot-worked grains were deformed by the prismatic 〈a〉 slip dominantly. The strain evolution analysis indicated that the multilayered structure relaxed the strain localization via strain transfer from the DRXed to the hot-worked regions, which led to the high ductility of the alloy. Precipitation of the γ′ on basal planes and the β′ phases on the prismatic planes of the α-Mg generated closed volumes, which enhanced the strength by pinning dislocations effectively, and contributed to the high ductility by impeding the propagation of micro-cracks inside the grains. The deformation incompatibility between the hot-worked grains and the arched block-shaped long-period stacking ordered (LPSO) phases induced the crack initiation and propagation, which fractured the alloy.

Microstructure and Mechanical Property of Mg-13Gd-0.2Ni Alloy Processed by Extrusion and Aging

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Microstructure and Mechanical Properties of Moderate-Speed Extrudable Mg-Gd-Sm-Zr Alloy

Microstructures and Mechanical Properties of Mg-10Gd-3Y-2Zn-0.5Zr Alloy

The Development of a High-Strength Mg-10.3Gd-4.4Y-0.9Zn-0.7Mn Alloy Subjected to Large Differential-Thermal Extrusion and Isothermal Aging

Fine-grained Mg–1Mn–0.5Al–0.5Ca–0.5Zn alloy with high strength and good ductility fabricated by conventional extrusion

Achieving ultrahigh strength in pre-ageing-extruded Mg-Gd-Y-Zn-Mn alloys via ageing treatment

A high-strength low-rare-earth-alloyed magnesium alloy via traditional hot-extrusion

An alternating ageing-annealing process for enhancing strength and ductility of a Mg-Gd-Y-Zn-Zr alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Y Alloy

A Super High-Strength Mg-Gd-Y-Zn-Mn Alloy Fabricated by Hot Extrusion and Strain Aging

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Aging characteristics and mechanical properties of cast and wrought MG-11GD-2ND-0.5ZR alloys

Preparation of high-performance Mg-Gd-Y-Mn-Sc alloy by heat treatment and extrusion

High Strength and Ductility Mg-8Gd-3Y-0.5Zr Alloy with Bimodal Structure and Nano-Precipitates

Microstructural evolution and enhanced mechanical properties of Mg–Gd–Y–Zn–Zr alloy via centrifugal casting, ring-rolling and aging

Fabrication of magnesium alloy with high strength and heat-resistance by hot extrusion and ageing

Effect of Aging Treatment on the Microstructure, Fracture Toughness and Fracture Behavior of the Extruded Mg-7Gd-2Y–1Zn-0.5Zr Alloy