Influence of minor RE addition on microstructures, tensile properties, and creep resistance in a die-cast Mg–Al–Ca–Mn alloy
Deping Zhang,Boqiong Li,Jinhui Zhang,Ting Niu,Chunlin Li,Peng Cheng,Liuqing Yang
DOI: https://doi.org/10.1016/j.jmrt.2023.07.265
IF: 6.267
2023-08-24
Journal of Materials Research and Technology
Abstract:In this work, we have investigated the influence of RE content on the tensile property, creep resistance, and microstructures of a die-cast Mg–9Al-0.3Ca-0.2Mn (wt. %). Minor content of RE elements simultaneously increases the strength and ductility, which is mostly since RE addition refined primary dendritic α-Mg and eutectic α-Mg matrix and eutectic β -Mg 17 Al 12 phases and formed thermally stable Al 11 RE 3 phases. The 0.6% RE adding alloy obtains the best strength-ductility synergy along with the UTS of 245 MPa, TYS of 170 MPa, and EL of 5.7%. The 0.6−1.0% RE addition gives rise to a reduction of the minimum creep rate by over one order of magnitude of the alloy, indicating a significant enhancement in creep resistance, which can be mainly attributed to RE addition introducing Al 11 RE 3 phases to prevent grain boundary sliding, and suppressing dynamic precipitation of γ-Mg 17 Al 12 phases during high-temperature creep. These results can provide important references for the design of creep-resistant die-cast Mg alloys and promote the application of commercial Mg–Al based alloys at high temperatures.
materials science, multidisciplinary,metallurgy & metallurgical engineering