High Temperature Creep Behavior of Mg-6Al-1Zn-1.8Gd-0.9Y Alloy

CHEN Xiaoya,LI Quan'an,CHEN Jun,ZHANG Qing,SONG Xiaojie,JIANG Huizhen

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2016.06.025

2016-01-01

Abstract:The high temperature creep behavior of Mg-6Al-1Zn-1.8Gd-0.9Y alloy was analyzed.The results show that the creep value of the alloy is 0.86％ at 50MPa and 150 ℃.The steady state creep rate is 1.8×10-8 s-1,After heat treatment,the creep value of the alloy in 50MPa and 150℃ is 0.36％ and the steady state creep rate is 8.9×10-9s-1,which can satisfy the use requirement at high temperature the creep activation energy of the as-cast alloy is 24.3 kJ/mol in 50MPa.After heat treatment,the creep activation energy of the alloy in 50 MPa and 70 MPa is 23.4 kJ/mol and 34.3 kJ/mol,respectively,which is closed to the grain boundary sliding activation.