Effect of Quasicrystal I-Phase on Microstructure and Mechanical Properties of Hot-Rolled Diphasic Mg-8 Wt.% Li Alloy

Cai Xiang,Wang Zan,Wang Xinyi,Qiao Yanxin,Xu Daokui,Zhou Jian,Xue Feng
DOI: https://doi.org/10.1007/s11665-021-06406-8
IF: 2.3
2021-01-01
Journal of Materials Engineering and Performance
Abstract:The microstructure and mechanical properties of hot-rolled Mg-8 wt.% Li and Mg-8 wt.% Li-6 wt.% Zn-1.2 wt.% Y alloys were investigated, and it was demonstrated that due to the formation of the I-phase (Mg 3 Zn 6 Y, icosahedral structure), the crystallographic texture and strength of the alloys is weakened and increased, respectively. At different hot-rolled ratios, the anisotropy (plasticity) of Mg-8 wt.% Li alloy exhibits obviously stronger than the Mg-8 wt.% Li-6 wt.% Zn-1.2 wt.% Y alloy. Failure analysis indicated that ductile fracture occurs along the rolling direction (RD), while quasi-cleavage fracture occurs along the transverse direction (TD). Cracks in the Mg-8 wt.% Li were found to be mainly initiated at the α -Mg phase and the two-phase boundary, which were respectively generated by tensile testing along the RD and TD. The cracks in the Mg-8 wt.% Li-6 wt.% Zn-1.2 wt.% Y alloy were confirmed to be located in the rich I-phase region of the α -Mg phase and at the junction site of the matrix phases.
What problem does this paper attempt to address?