Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Effect of quasicrystal and Laves phases on strength and ductility of as-extruded and heat treated Mg–Zn–Gd-based alloys

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Effects of extrusion on the microstructure and mechanical properties of Mg–Zn–Gd alloy reinforced with quasicrystalline particles

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Effect of Annealing on Microstructure and Tensile Properties of As-Extruded Mg-5Gd-4Y-0.5Zn-0.5Zr Alloy

Effects of Icosahedral Phase on Mechanical Anisotropy of As-Extruded Mg-14Li (in Wt%) Based Alloys

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Effect of Ca Concentration on Microstructure and Mechanical Properties of As-Cast and As-Extruded Quasicrystal-Strengthened Mg-7.2Zn-2.4Gd Alloy

Effect of Icosahedral Phase on Crystallographic Texture and Mechanical Anisotropy of Mg–4%Li Based Alloys

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Improved Ductility of Mg–3Gd–0.6Zr Alloy by Cuboid-Shaped Phase: Experiments and First-Principle Calculations

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Microstructure evolution difference in Mg96.5Gd2.5Zn1 alloys extruded from as-cast and solution-treated states

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Effect of Zn/(Gd+Y) ratio on the microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

Investigation of the optimum preheating treatment parameters for extruded Mg–Gd–Y–Zn–Zr alloy using high-throughput experiments

Microstructure and mechanical properties synergistically enhanced via heat treatment modification of the as-extruded Mg-1.5Al-0.5Zn-0.2Y-0.2Ca alloy

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States