Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Effects of Icosahedral Phase on Mechanical Anisotropy of As-Extruded Mg-14Li (in Wt%) Based Alloys

Effect of Icosahedral Phase on Crystallographic Texture and Mechanical Anisotropy of Mg–4%Li Based Alloys

Effect of Icosahedral Phase on the Crystallographic Texture and Mechanical Anisotropy of Duplex Structured Mg–Li Alloys

Effect of Icosahedral Quasicrystalline Fraction and Extrusion Ratio on Microstructure, Mechanical Properties, and Anisotropy of Mg-Zn-Gd-Based Alloys

The Strengthening Effect of Icosahedral Phase on As-Extruded Mg–Li Alloys

Effect of Microstructure and Texture on the Mechanical Properties of the As-Extruded Mg–Zn–Y–Zr Alloys

Ex-situ EBSD Analysis of Yield Asymmetry, Texture and Twinning Development in Mg–5Li–3Al–2Zn Alloy During Tensile and Compressive Deformation

Microstructure, Texture, and Mechanical Properties of As-Extruded Mg-xLi-3Al-2Zn-0.2Zr Alloys (x = 5, 7, 8, 9, 11 Wt%)

Effect of Quasicrystal I-Phase on Microstructure and Mechanical Properties of Hot-Rolled Diphasic Mg-8 Wt.% Li Alloy

Effect of Extrusion Ratio on Microstructure, Texture, and Mechanical Properties of Dual-Phase Mg−8Li−6Zn−2Gd Alloy

The Effect of Y/Er and Zn Addition on the Microstructure and Mechanical Properties of Mg-11Li Alloy

Microstructure and Tensile Properties of As-Extruded Mg–Li–Zn–Gd Alloys Reinforced with Icosahedral Quasicrystal Phase

Microstructure, Texture Evolution and Tensile Properties of Extruded Mg-4.58Zn-2.6Gd-0.16Zr Alloy

Effect of quasicrystal and Laves phases on strength and ductility of as-extruded and heat treated Mg–Zn–Gd-based alloys

Effects of Zn and Gd Contents and Their Ratios on Microstructure and Mechanical Properties of As-Cast and As-Extruded Mg−8Li Alloys

Effect of Li Content on Microstructure, Texture and Mechanical Behaviors of the As-Extruded Mg-Li Sheets

Effects of Li Content on Phase Evolution and Mechanical Properties of Mg-xLi-6Zn-1.5Y Alloy

Microstructure Characterization and Mechanical Properties of the As-Cast and As-Extruded Mg-xLi-5Zn-0.5Er (x = 8, 10 and 12 Wt%) Alloys

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructural Evolution and Mechanical Properties of As‐Cast and As‐Extruded Mg–14Li Alloy with Different Zn/Y and Zn/Gd Addition

Effects of Icosahedral Phase Formation on the Microstructure and Mechanical Improvement of Mg Alloys: A Review