Inhibiting Effect of I-phase Formation on the Plastic Instability of the Duplex Structured Mg-8Li-6Zn-1.2Y (in Wt.%) Alloy

B. J. Wang,D. K. Xu,X. Q. Zhuang,L. Y. Sheng

DOI: https://doi.org/10.1016/j.jma.2021.08.030

IF: 11.813

2023-01-01

Journal of Magnesium and Alloys

Abstract:In this work, the tensile behaviors of Mg-8%Li and Mg-8%Li-6%Zn-1.2%Y alloys at ambient temperature were investigated and compared.It revealed that the plastic instability of Mg-8%Li alloy was quite remarkable and the variation range of serrated flowing stress can reach5 MPa. For the Mg-8%Li-6%Zn-1.2%Y alloy, the formation of I-phase（Mg3Zn6Y） can simultaneously enhance the tensile strength and eliminate the plastic instability phenomenon, whilst its ductility was degraded. The in-situ tensile tests revealed that for the Mg-8%Li alloy,the severity and number of slip traces present in both α-Mg and β-Li matrix phases increased remarkably with the applied tensile strain.However, slip traces were quite fine in β-Li matrix phase and could be clearly observed when the applied tensile strain exceeded 18%.Due to the incompatibility of plastic deformation occurred in two matrix phases, the induced strain concentration at α-Mg/β-Li interfaces caused their subsequent cracking. For the Mg-8%-6%Zn-1.2%Y alloy, the I-phase distributed at α-Mg/β-Li interfaces suppressed the plastic deformation of α-Mg matrix phase and the tensile strain was dominated by the β-Li matrix phase, resulting in the disappearance of plastic instability. Moreover, the plastic strain would preferentially concentrate at I-phase/β-Li interfaces and subsequently induced the cracking of I-phase.