DAMAGE BEHAVIOR OF TUNGSTEN TARGETS FOR 6 MEV LINEAR ACCELERATORS

Zhihui Wang,Zening Liu,Jiaru Shi,Hao Zha

DOI: https://doi.org/10.18429/jacow-ipac2019-thprb055

2019-01-01

Abstract:The target in electron linear accelerator is subjected to high-frequency and intense thermal shocks. Elevated temperatures in the target may lead to target recrystallization, fatigue cracking, creep and vaporization. In this study, experiments were carried out to investigate the damage behaviour of tungsten targets in 6 MeV linear accelerators under pulsed electron beam. The results show that recrystallization occurs after loading 6 MeV electron beam with repetition frequency of 220 Hz, pulse width of 4 μs and mean current of 151 μA for 248 s. Deformation and cracking caused by recrystallization are observed on the surface of the target. INTRODUCTION Medical linear accelerators are the most commonly used device for external beam radiation treatments for patients with cancer [1]. The X-ray target is a very important component at the end of the accelerating tube to produce highenergy X-ray. Pulsed electron beam deposits large amounts of heat within the target. The target exposed to high-frequency thermal shocks is at risks of damage, limiting the accelerator’s ability to deliver high-dose-rate X-ray irradiation. Literature review shows several possible damage forms of the most commonly used tungsten targets [2-5]: (1) Recrystallization. Recrystallization temperature of pure tungsten is reported to be 1300-1500 °C. After recrystallization, the crystal structures of tungsten atoms change, causing the changes in the macro-properties. Micro-cracks initiate and propagate along grain boundaries. Besides, embrittlement happens with the ductile brittle transition temperature (DBTT) rising from 70 °C to 230-280 °C. (2) Fatigue cracking. Pulsed electron beam causes highfrequency thermal shocks on the target. Cyclic temperature variations lead to alternating stress and further mechanical fatigue of the target. As the temperature cycles cross the DDTT frequently, tungsten target shifts between flexible and brittle, easily initiating cracking and even failing. (3) Melting and vaporization. The melting point of tungsten is 3410 °C. Melting occurs when the energy deposited on the surface of tungsten exceeds its melting threshold with temperature lower than the melting point. Concomitant phenomenon including fondant motion, droplet sputtering and vapour layer formation will also damage the target. Research shows tungsten block initiates melting under heat load of 2 GW/m3 for 2 ms. Experiments need to be done to figure out the damage behaviour of tungsten target in accelerators to ensure stable operation of the accelerator and to get greater X-ray yield.