Abstract:We report a systematic computational analysis of the mechanical behavior of plasma-facing component (PFC) tungsten focusing on the impact of void and helium (He) bubble defects on the mechanical response beyond the elastic regime. Specifically, we explore the effects of porosity and He atomic fraction on the mechanical properties and structural response of PFC tungsten, at varying temperature and bubble size. We find that the Young modulus of defective tungsten undergoes substantial softening that follows an exponential scaling relation as a function of matrix porosity and He atomic content. Beyond the elastic regime, our high strain rate simulations reveal that the presence of nanoscale spherical defects (empty voids and He bubbles) reduces the yield strength of tungsten in a monotonically decreasing fashion, obeying an exponential scaling relation as a function of tungsten matrix porosity and He concentration. Our detailed analysis of the structural response of PFC tungsten near the yield point reveals that yielding is initiated by emission of dislocation loops from bubble/matrix interfaces, mainly 1/2⟨111⟩ shear loops, followed by gliding and growth of these loops and reactions to form ⟨100⟩ dislocations. Furthermore, dislocation gliding on the ⟨111⟩{211} twin systems nucleates 1/6⟨111⟩ twin regions in the tungsten matrix. These dynamical processes reduce the stress in the matrix substantially. Subsequent dislocation interactions and depletion of the twin phases via nucleation and propagation of detwinning partials lead the tungsten matrix to a next deformation stage characterized by stress increase during applied straining. Our structural analysis reveals that the depletion of twin boundaries (areal defects) is strongly impacted by the density of He bubbles at higher porosities. After the initial stress relief upon yielding, increase in the dislocation density in conjunction with decrease in the areal defect density facilitates the initiation of dislocation-driven deformation mechanisms in the PFC crystal.

Evolution of tungsten degradation under different cyclic ELM-like high heat flux plasma

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Dependence of Tungsten Crack Behaviors on Heat Source Parameters under Transient Heat Flow

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Microstructure-based crack formation in tungsten exposed to cyclic transient heating

Progress of High Heat Flux Component Manufacture and Heat Load Experiments in China

Experimental and simulation studies on damage mechanisms of tungsten and molybdenum under compressed plasma flow irradiation

HIGH HEAT LOAD PROPERTIES OF W/Cu FUNCTIONALLY GRADED MATERIALS

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Damages on Pure Tungsten Irradiated by Compression Plasma Flows

Recent Studies of Tungsten-Based Plasma-Facing Materials in the Linear Plasma Device STEP

Surface Damage and Structure Evolution of Recrystallized Tungsten Exposed to Elm-Like Transient Loads

Plasma and X-ray radiation-induced damage mechanisms in a tungsten heavy alloy

Fem Study of Recrystallized Tungsten under Elm-Like Heat Loads

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Microstructural modification of highly porous resolidified tungsten in heat flux of 46.3 GW/m 2 and focused ion beam

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Molecular-Dynamics Analysis of the Mechanical Behavior of Plasma-Facing Tungsten