Abstract:We report a systematic computational analysis of the mechanical behavior of plasma-facing component (PFC) tungsten focusing on the impact of void and helium (He) bubble defects on the mechanical response beyond the elastic regime. Specifically, we explore the effects of porosity and He atomic fraction on the mechanical properties and structural response of PFC tungsten, at varying temperature and bubble size. We find that the Young modulus of defective tungsten undergoes substantial softening that follows an exponential scaling relation as a function of matrix porosity and He atomic content. Beyond the elastic regime, our high strain rate simulations reveal that the presence of nanoscale spherical defects (empty voids and He bubbles) reduces the yield strength of tungsten in a monotonically decreasing fashion, obeying an exponential scaling relation as a function of tungsten matrix porosity and He concentration. Our detailed analysis of the structural response of PFC tungsten near the yield point reveals that yielding is initiated by emission of dislocation loops from bubble/matrix interfaces, mainly 1/2⟨111⟩ shear loops, followed by gliding and growth of these loops and reactions to form ⟨100⟩ dislocations. Furthermore, dislocation gliding on the ⟨111⟩{211} twin systems nucleates 1/6⟨111⟩ twin regions in the tungsten matrix. These dynamical processes reduce the stress in the matrix substantially. Subsequent dislocation interactions and depletion of the twin phases via nucleation and propagation of detwinning partials lead the tungsten matrix to a next deformation stage characterized by stress increase during applied straining. Our structural analysis reveals that the depletion of twin boundaries (areal defects) is strongly impacted by the density of He bubbles at higher porosities. After the initial stress relief upon yielding, increase in the dislocation density in conjunction with decrease in the areal defect density facilitates the initiation of dislocation-driven deformation mechanisms in the PFC crystal.

Damages on Pure Tungsten Irradiated by Compression Plasma Flows

Experimental and Numerical Simulations of ELM-like Transient Damage Behaviors to Different Grade Tungsten and Tungsten Alloys

Experimental and simulation studies on damage mechanisms of tungsten and molybdenum under compressed plasma flow irradiation

Dependence of Tungsten Crack Behaviors on Heat Source Parameters under Transient Heat Flow

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Evolution of tungsten degradation under different cyclic ELM-like high heat flux plasma

Recent Studies of Tungsten-Based Plasma-Facing Materials in the Linear Plasma Device STEP

Microstructural modification of highly porous resolidified tungsten in heat flux of 46.3 GW/m 2 and focused ion beam

Plasma-facing Components Damage and Its Effects on Plasma Performance in EAST Tokamak

Surface Cracking of Tungsten-Vanadium Alloys under Transient Heat Loads

Manufacturing of magnetron sputtering tungsten coatings and irradiation damage behavior under helium plasma exposure

Microstructure-based crack formation in tungsten exposed to cyclic transient heating

Elastic Properties of Plasma-Exposed Tungsten Predicted by Molecular-Dynamics Simulations

Review of Irradiation Damage Behavior of Tungsten Exposed to Plasma in Nuclear Fusion

Corrosion and Microstructure Evolution of He+ Plasma Irradiated Tungsten PFMs

Erosion dynamics of tungsten fuzz during ELM-like heat loading

Progress in Irradiation Damage of Tungsten and Tungsten Alloys Under Different Irradiation Particles

Plasma and X-ray radiation-induced damage mechanisms in a tungsten heavy alloy

Thermal Conductivity Degradation and Recovery in Ion Beam Damaged Tungsten at Different Temperature

Corrosion and microstructure evolution of He plus plasma irradiated tungsten PFMs

Molecular-Dynamics Analysis of the Mechanical Behavior of Plasma-Facing Tungsten