Abstract:A comprehensive modeling framework for the thermoforming of polymer matrix woven laminate composite was developed. Two numerical indicators, the slip path length and traction magnitude, have been identified to be positively correlated to matrix smearing and wrinkling defects. The material model has been calibrated with picture-frame experimental results, and the prediction accuracy for intra-ply shear and thickness distribution was examined with measurements of the physically formed parts. Specifically, thickness prediction for most locations on the formed parts was accurate within an 11.6% error margin. However, at two points with significant intra-ply shear, the prediction errors increased to around 20%. Finally, a parametric study was conducted to determine the relationship between various process parameters and the quality of the formed part. For the trapezoidal part, orienting the laminate at 45 degrees to the mold axis reduces the likelihood of matrix smear and wrinkling defects. Although this laminate orientation yielded a greater spatial variation in part thickness, the thickness deviation is lower than that for the 0-degree orientation case. Two forming analyses were conducted with ramp rates of 25 mm/s and 80 mm/s to match the equipment's operational limits. It was observed that higher forming rates led to a greater likelihood of defects, as evidenced by a 15% and 10% increase in the formed part areas with longer slip paths and higher traction magnitudes, respectively. It was discovered that shallower molds benefit from faster ramp rates, while deeper molds require slower rates to manage extensive shearing, stretching and bending. Faster forming rates lead to smaller thickness increases at high intra-ply shear regions, indicating a shift from intra-ply shear to out-of-plane bending due to the visco-plastic effect of the molten laminate and can negatively impact part quality. Lastly, it was shown that a well-conceived strategy using darts could improve the part quality by reducing the magnitude of the defect indicators.

Characterisation of bending mechanics in uncured laminated materials using a modified Dynamic Mechanical Analysis

Multi-Scale Modelling of Long-Term Mechanical Behaviour in Polymer Composite Laminates with Woven Fibre Architecture

Understanding the Impact of Fibre Wrinkle Architectures on Composite Laminates Through Tailored Gaps and Overlaps

Dynamic Mechanical Analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process

Investigation of the curing behaviour of carbon fibre epoxy prepreg by Dynamic Mechanical Analysis DMA

Thermo-Chemo-Mechanical Modeling of Residual Stress in Unidirectional Carbon Fiber-Reinforced Polymers during Manufacture

Modeling on the Effect of Automated Fiber Placement Induced Gaps in Curved Composite Laminates

Numerical modeling for curing of unidirectional carbon fiber reinforced polymer based on micromechanics in Laplace domain

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

On the relevance of modeling viscoelastic bending behavior in finite element forming simulation of continuously fiber reinforced thermoplastics

3D FEA Modelling of Laminated Composites in Bending and Their Failure Mechanisms

Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by Dynamic Mechanical Analysis (DMA)

Experimental characterisation and constitutive modelling of the intra-ply tensile and shear properties of unidirectional fibre reinforced thermoplastics (UD FRTPs) under solid-state stamp forming conditions

The use of discontinuous PEEK/carbon fiber thermoplastic moulding compounds for thick-section componentry

A Modeling Framework for the Thermoforming of Carbon Fiber Reinforced Thermoplastic Composites

Performance Evaluation of Out-of-Spec Carbon Prepregs for Upcycling Purposes

Experimental study on the mechanical behavior of laminates made by fiber steering: Influence of fiber angle and tow width

Experimental Investigation on Deformation and Strength of Carbon/epoxy Laminated Curved Beams

Bimodulus constitutive models and the simulation on bending properties of woven carbon fibre-reinforced composites

Damage-Caused Residual Curvatures in Symmetric Cross-Ply Laminates

Damage Analysis of Carbon Fiber-Reinforced Thermoplastic Laminates under Bending Based on Acoustic Emission and Digital Image Correlation