Dynamic Mechanical Analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process

W. Stark,M. Jaunich,J. McHugh

DOI: https://doi.org/10.1016/j.polymertesting.2014.11.004

IF: 5.1

2015-02-01

Polymer Testing

Abstract:Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E′, loss modulus E″ and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.

materials science, characterization & testing,polymer science