Abstract:The present experimental study assesses the mechanical properties of glass/carbon/glass hybrid composite laminates after being exposed to moisture in a deep freezer and elevated temperatures for extended periods. The top and bottom layers of the hybrid laminates are reinforced with glass fibre, and the middle layer is reinforced with carbon fibre using the epoxy matrix as a binder polymer material. The hybrid laminates were manufactured using the resin transfer moulding method, and their compressive and tensile properties were determined using a tensile testing machine. The storage modulus, loss modulus, and damping factors of all groups of laminates were identified using a dynamic mechanical analysis as a function of temperature and vibration frequency. The experimental results on compressive and tensile properties revealed slight variations when the hybrid laminates were kept at low temperatures in a deep freezer for extended periods. This might occur due to the increasing molecular crosslinking of the polymer network. As the testing temperature increased, compressive, tensile, storage modules, loss modulus, and damping factors decreased. This might occur due to the increasing mobility of the binder material. Particularly, the highest stiffness parameters were obtained at −80 °C/GCG (glass/carbon/glass) laminates due to the presence of a beta transition in the glassy region. The relationships between the glass transitions and the targeted frequencies were characterized. The values of the glass transition shift towards higher temperatures as the frequency increases. This might occur due to a reduction in the gaps between the crosslinking of the epoxy network when the frequency increases. The accuracy of the storage modulus results was compared with the empirical models. The model based on the Arrhenius law provided the closest correlation. Meanwhile, another model was observed that was not accurate enough to predict when gamma and beta relaxations occur in a glassy state.

Carbon-fibre epoxy prepreg (CFC) curing in an autoclave analogue process controlled by Dynamic Mechanical Analysis (DMA)

Dynamic Mechanical Analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process

Investigation of the curing behaviour of carbon fibre epoxy prepreg by Dynamic Mechanical Analysis DMA

Dynamic Mechanical Analysis of the Curing of Carbon Fiber/bismaleimide Resin Prepreg

Study of Post-curing Properties of Wood Flour Reinforced Phenolic Molding Materials

Performance Evaluation of Out-of-Spec Carbon Prepregs for Upcycling Purposes

Curing Kinetics and Mechanical Properties of the Epoxy Vitrimer Based on Transesterification and Its Composite Laminates

A New Method to Characterize the Cure State of Epoxy Prepreg by Dynamic Mechanical Analysis

Direct Measurement of Cure‐Induced Stress in Thermosetting Materials by Means of a Dynamic Mechanical Analyzer

Characterisation of bending mechanics in uncured laminated materials using a modified Dynamic Mechanical Analysis

Magnetic Fiber Enabled Curing Electrogram: Real-time Process Monitoring for Thermosetting Polymer Materials

Quick Preparation of Moisture-Saturated Carbon Fiber-Reinforced Plastics and Their Accelerated Ageing Tests Using Heat and Moisture

Assessment of E‐glass/epoxy prepreg aging via analytical, physical and mechanical techniques

The Curing Kinetics of E-Glass Fiber/Epoxy Resin Prepreg and the Bending Properties of Its Products

Dielectric and rheological study of the molecular dynamics during the cure of an epoxy resin

Study of the curing process of carbon fiber reinforced resin matrix composites in autoclave processing

Cure Kinetics Modeling of a High Glass Transition Temperature Epoxy Molding Compound (EMC) Based on Inline Dielectric Analysis

Influence of Long-Term Moisture Exposure and Temperature on the Mechanical Properties of Hybrid FRP Composite Specimens

Effects of storage aging on the cure kinetics of T700/BMI prepregs

Thermal Characterization of Carbon‐nanofiber‐reinforced Tetraglycidyl‐4,4′‐diaminodiphenylmethane/4,4′‐diaminodiphenylsulfone Epoxy Composites

Comparison by thermal analysis of Joule-cured versus oven-cured composites