Abstract:With the rapid development of the third-generation semiconductor materials, an appropriate high-temperature-resistant die attach material has become one of the bottlenecks to fully exploit the excellent properties of the third-generation semiconductor power devices. At the same time, a low-bonding temperature is always the pursuit goal of packaging engineers to reduce the thermal residual stress in electronic devices. In this paper, a low-temperature bonding method was proposed to address the above-mentioned issue based on In infiltrating the nanoporous Cu. In, as a low melting point metal, can significantly reduce the bonding temperature, and the nanoporous Cu structure can provide a very large specific surface area, which greatly increases the consumption rate of In. Furthermore, the formed Cu-In IMCs with high-remelting temperature can withstand the high operating temperature. The microstructures of the bondlines before and after bonding were studied in detail. The results show that the bondline can completely consume the low melting point In, within 10 min at 165 °C under a pressure of 0.75 MPa. When the bonding temperature was further increased to 310 °C, the bondline was composed of η-Cu2In and δ-Cu7In3 phases, whose melting points were more than 600 °C. The average electrical resistivity was determined to be 5.53 ± 0.65 μΩ cm, and the thermal conductivities were 144.33 W m−1 K−1, 139.24 W m−1 K−1 and 129.79 W m−1 K−1 at 30 °C, 150 °C and 300 °C, respectively. The average shear strength were 19.09 ± 3.4 MPa, 20.47 ± 4.6 MPa and 30.73 ± 5.2 MPa at 30 °C, 250 °C, 310 °C, respectively. These results indicate that the nanoporous Cu infiltrated with In could meet the requirements of electrical, thermal conduction, and mechanical support as a die attachment for high-power devices.

A Low-Temperature Cu-to-Cu Interconnection Method by Using Nanoporous Cu Fabricated by Dealloying Electroplated Cu–Zn

Low Temperature Cu-Cu Bonding Using Copper Nanoparticles Fabricated by High Pressure Pvd

Low Temperature Fine-Pitch Wafer-Level Cu-Cu Bonding Using Nanoparticles Fabricated by PVD

Thermal instability of nanocrystalline Cu enables Cu-Cu direct bonding in interconnects at low temperature

Interfacial Characterization of Low-Temperature Cu-to-Cu Direct Bonding with Chemical Mechanical Planarized Nanotwinned Cu Films

Low-temperature Cu Cu Direct Bonding with Ultra-Large Grains Using Highly (110)-Oriented Nanotwinned Copper

Low Temperature Cu-Cu Bonding Using an Intermediate Sacrificial Sn Layer

Cu-Cu Bonding By Ag Nanostructure At Low Temperature Of 180 Degrees C

A low-temperature bonding method for high power device packaging based on In-infiltrated nanoporous Cu

Low Temperature Fine-pitch Cu-Cu Bonding Using Au Nanoparticles As Intermediate

Low Temperature Cu-Cu Bonding Using Ag Nanostructure for 3d Integration

Cu-Cu bonding by Ag nanostructure at low temperature of 180 °C

Low-Temperature Cu-Cu Bonding Using Silver Nanoparticles Fabricated by Physical Vapor Deposition

Enhanced Cu-Cu bonding for ultrahigh-density interconnection: Co passivation bonding with non-oxidation interfaces

Low Contact Resistance Copper-Copper Bonding with Selective Electroless Plating Cobalt Interlayer

Low Temperature Cu-Cu Bonding Using Ag Nanoparticles By Pvd

Low-Temperature Copper Bonding Strategy with Graphene Interlayer

Low-Temperature and CMP-Free Direct Bonding of Porous Cu Bumps

Cu-Cu joint formation by low-temperature sintering of self-reducible Cu nanoparticle paste under ambient condition

Low temperature solid-state-diffusion bonding for fine-pitch Cu/Sn/Cu interconnect

Low temperature Cu bonding with large tolerance of surface oxidation