Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Quantitative Relationship Between the Density and Structural Unit of Alpha Alumina Prepared from Gibbsite and Boehmite

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Preparation and properties of high-purity porous alumina support at low sintering temperature

The Preparation and Properties of Alumina Ceramics Through a Two-Step Pressureless Sintering Process

Effect of Seedings on the Microstructure of Hydrated Alumina

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Reactive Crystallization Kinetics Study of Boehmite in Ammonia Solution by Adding Ammonium Aluminum Sulfate

Pore structure of aluminas derived from the alkyl derivatives of boehmite

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

High Temperature Thermal Stability of Al2O3 Modified by BaO

EFFECTS OF PREPARATION METHOD AND VARIOUS MODIFIERS ON THE THERMAL STABILITY OF ALUMINA

One-step preparation of high-purity boehmite by the effect of sugar alcohol in the aluminum-water reaction

Study of Gamma Alumina Synthesis – Analysis of the Specific Surface Area

The Fabrication of Porous Mullite Ceramics Based on the Different Sizes of Aluminum Hydroxide

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Enhanced Thermal Stability and High-Quality of Α-Alh3 Via Crystal Seed Preparation Method

Boehmite Preparation via Alditols-Interacting Transformation of Metastable Intermediates in Al–H2O Reaction Crystallization

Hydrothermal stability of gamma-Al 2 O 3 supports varied with crystal plane orientation of pseudo-boehmite precursor

Preparation and characterisation of boehmite precursor and sinterable alumina powder from aqueous aluminium chloride-urea reaction