Abstract:The dissolution of boehmite is a technical issue for Al industry because of its recalcitrant nature. In fact, a similar problem exists with boehmite in nuclear waste sludge at the Hanford site in Eastern Washington State, USA. Dissolution of Al phases is required to reduce the waste loadings in the final borosilicate glass waste form. Although not the most common Al-bearing species in the sludge, boehmite may become a rate limiting step in the processing of the wastes. Hanford boehmite is an order of magnitude more resistant to dissolution in hot caustic solutions than expected from surface-normalized rates. We are exploring potential intrinsic and extrinsic effects that may limit boehmite reactivity; one clue comes from microstructural analyses that indicate an association of Cr with Al in the Hanford nuclear waste. Hence, in this first paper, we investigated the potential role of chromium on the reactivity of boehmite in caustic solution. An important finding was that irrespective of the synthesis pathway, amount of Cr(III), or the resultant morphology, there was no evidence for Cr incorporation in the bulk structure, in agreement with QM calculations. In fact, electron microscopic (EM) and spectroscopic analyses showed that Cr was enriched at the (101) edges of the boehmite. However, Cr had no measurable effect on the morphology during the synthesis step. In contrast, comparison of the morphologies of the synthetic Cr-doped and pure boehmite samples after exposure to caustic solutions provided evidence that Cr inhibited the corrosion. TEM showed that Cr was not homogeneously distributed at the surface. Consequently, Cr may have partially passivated the surface by blocking discrete energetic sites on the lateral surfaces of boehmite.

Reactive Crystallization Kinetics Study of Boehmite in Ammonia Solution by Adding Ammonium Aluminum Sulfate

Boehmite Preparation via Alditols-Interacting Transformation of Metastable Intermediates in Al–H2O Reaction Crystallization

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Preparation of pseudo-boehmite via carbonation of sodium aluminate lixivium extracted from coal fly ash

Secondary Nucleation and Growth Kinetics of Aluminum Hydroxide Crystallization from Potassium Aluminate Solution

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

A new route to synthesis of γ-alumina nanorods

Transformation Behavior of Gibbsite to Boehmite by Steam-Assisted Synthesis

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Relationship between formation conditions, properties, and crystallite size of boehmite

Effect of Seedings on the Microstructure of Hydrated Alumina

Can Cr(III) Substitute for Al(III) in the Structure of Boehmite

Study on Preparation and Characterization of gamma-Al(2)O(3) from Coal Fly Ash

One-step preparation of high-purity boehmite by the effect of sugar alcohol in the aluminum-water reaction

Thermodynamics and kinetics of alumina extraction from fly ash using an ammonium hydrogen sulfate roasting method

Preparation and characterisation of boehmite precursor and sinterable alumina powder from aqueous aluminium chloride-urea reaction

New sol-gel route using inorganic salt for synthesizing Al2O3 nanopowders

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

Extraction of alumina from high-alumina fly ash by ammonium sulfate: roasting kinetics and mechanism

Morphology Evolution in Hydrothermal Synthesis of Mesoporous Alumina

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method