Abstract:The aluminum oxyhydroxide boehmite is an important crystalline phase in nature and industry. We report development of a flexible additive-free hydrothermal synthesis method to prepare high quality boehmite nanoplates with sizes ranging from under 20 nm 5 mu m to via using hydrated alumina gels and aluminum hydroxide amorphous powders as precursors. The size and morphology of the boehmite nanoplates was systematically varied between hexagonal and rhombic by adjusting precursor concentrations, pH, and the synthesis temperature, due to face-specific effects. The transformation mechanism is consistent with dissolution and reprecipitation, and involves transitory initial appearance of metastable gibbsite that is later consumed upon nucleation of boehmite. Detailed X-ray pair distribution characterization of the solids over time showed similarities in short-range order that suggest linkages in local chemistry and bonding topology between the precursors and product boehmite, yet also that precursor-specific differences in long-range order appear to manifest subtle changes in resulting boehmite characteristics, suggesting that the rate and extent of water release or differences in the resulting solubilized aluminate speciation lead to slightly different polymerization and condensation pathways. The findings suggest that, during dissolution of the precursor, precursor-specific dehydration or solution speciation could be important aspects of the transformation impacting the molecular-level details of boehmite nucleation and growth.

Morphological Controlled Growth of Nanosized Boehmite with Enhanced Aspect Ratios in an Organic Additive-Free Cationic–Anionic Double Hydrolysis Method

Size and Morphology Controlled Synthesis of Boehmite Nanoplates and Crystal Growth Mechanisms

Growth Of Boehmite Nanoribers By Assembling Nanoparticles With Surfactant Micelles

Different nanostructures of boehmite fabricated by hydrothermal process: effects of pH and anions

Effects of pH and ions on the morphological evolution of boehmite prepared by hydrothermal treatment of ultrafine Bayer gibbsite

Hydrothermal Preparation Of Boehmite Nanorods By Selective Adsorption Of Sulfate

Spontaneous Formation of Nano‐fibrillar Boehmite and the Enhancement Effect of Polyethylene Glycol

Organic-free Synthesis of Boehmite Nanofibers by Al2(SO4)3·18H2O with High Pore Volume

Morphology Controllable Synthesis Of Gamma-Alumina Nanostructures Via An Ionic Liquid-Assisted Hydrothermal Route

Facile Synthesis of Hierarchical Flower-Like Γ-Alooh Films Via Hydrothermal Route on Quartz Surface

From Al4B2O9nanorods to AlOOH (boehmite) Hierarchical Nanoarchitectures

Formation of hierarchical boehmite with different nanostructures in dry-gel conversion process

Manipulating the size and morphology of aluminum hydrous oxide nanoparticles by soft-chemistry approaches

Hydrothermal synthesis of boehmite nanorods from alumina sols

Hierarchical nanoarchitectonics of boehmite: The preparation of three-dimensional flower-like via hydrothermal method without surfactants

Growth and surface properties of boehmite nanofibers and nanotubes at low temperatures using a hydrothermal synthesis route.

Controlling the morphology of calcium sulfate hemihydrate using aluminum chloride as a habit modifier

Clean Synthesis of Hierarchically Structured Boehmite and Γ-Alumina with a Flower-Like Morphology

Hydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina

Effects of Cation on the Morphology of Boehmite Precipitated from Alkaline Solutions by Adding Gibbsite As Seed

Synthesis of Flower-Like Boehmite (Γ-Alooh) Via a One-Step Ionic Liquid-Assisted Hydrothermal Route