Abstract:Electrochemical impedance spectroscopy(EIS)was carried out on AM60 magnesium alloy specimens during 96 hour exposure periods into aerated 0.1mol/L NaCl,0.1mol/L Na2 SO4 and saturated Mg(0H)2 solutions.In the solutions containing C1-ions,the impedance spectroscopy takes on two capacitive loops in high frequency and middle frequency domain respedtively,while one inductive loop appears in first 36 hour immersion.The similar EIS behavior for AM60 in Na2 S04 solution had been observed,while the low frequency relaxation behavior is different.Comparing to the C1-ions,the S042-ions presented relatively weak corrosive ability.In the saturated Mg(OH)2 solution,due tO the anodic and cathodic reaction were restrained from the polarization curves by weak hydrolyzation of Mg(OH)2,the EIS behavior of AM60 differs from that in the other two aggressive ions solution.A relatively new method was applied to research the corrosion process with detail.Fractal dimension was calculated from the high frequency capacitive arc which was corresponding to the origin surface double electronic layer of AM60 magnesium in three kind solutions.The curves of fraetal dimension vs immersion time indicated that C1-ions presented the strongest corrosive attack,also shown the best self-repassivation behavior to recover the pits which.were produced by the existefiee of C1-ions.The SO42-ions attacked the surface of AM60,while the repassivation could be ignored.The increase of fractal dimension in Mg(OH)2 was mainly due to the adsorption of infusibility Mg(OH)2 on the surface increasing surface roughness.

ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF Al ALLOYS DURING EXFOLIATION CORROSION

Electrochemical impedance spectroscopy during corrosion process of 8090 Al-Li alloy in EXCO solution

Investigation of Exfoliation Corrosion of Rolled Aa8090 Al-Li Alloy Using Electrochemical Impedance Spectroscopy

Exfoliation Corrosion Susceptibility of 8090 Al-Li Alloy Examined by Electrochemical Impedance Spectroscopy

Exfoliation Corrosion of Aluminum Alloy AA7075 Examined by Electrochemical Impedance Spectroscopy

INFLUENCE OF TENSILE STRESS ON EXFOLIATION CORROSION AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF 7075al - ALLOY

Exfoliation Corrosion of Al-Li Alloy 2090-T6 in Exco Solution: A Study of Electrochemical Noise and Electrochemical Impedance Spectroscopy

Electrochemical Impedance Spectroscopy Analysis on Aluminum Alloys in EXCO Solution

EIS Investigation of the Deposition of Trivalent Chromium Coatings on Al 6063 Alloy

The Effect of Applied Tensile Stress on the Exfoliation Corrosion of 7075‐T6 Alloy

Electrochemical Impedance Spectra for the Corrosion of Porous Cu-35mass%Ni-(5,10)mass%Cr Alloys in Molten (0.62li,0.38k)2co3 at 650 °C in Air

REVIEW ON EXFOLIATION SUSCEPTIBILITY OF ALUMINIUM ALLOYS AND QUANTITATIVE MEASUREMENT METHOD

Electrochemical Impedance Spectroscopy Analysis on the Electrochemical Dissolution of Aluminum in an Alkaline Solution

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Electrochemical Impedance Fractal Study of AM60 Magnesium Alloy in Aggressive Solution

In-situ visualization of corrosion behavior of Al CoCrFeNi high-entropy alloys during electrochemical polarization

Understanding the Corrosion Behavior of the AZ91D Alloy in Simulated Body Fluid through the Use of Dynamic EIS

Exfoliation Corrosion of As-Extruded Mg–1Li–1Ca: the Influence of the Superficial Layer

Corrosion behavior of Al-6.8Zn-2.2Mg-Sc-Zr alloy with high resistance to intergranular corrosion

Synergistic Effects of Corrosion and Slow Strain Rate Loading on the Mechanical and Electrochemical Response of an Aluminium Alloy

STUDY ON THE CORROSION BEHAVIOR OF Ce CONVERSION COATINGS ON Al6061/SiCp COMPOSITES