Electrochemical Impedance Fractal Study of AM60 Magnesium Alloy in Aggressive Solution

ZHONG Li-ying,CAO Fa-he,LIU Wen-juan,ZHANG Zhao,ZHANG Jian-qing

2009-01-01

Abstract:Electrochemical impedance spectroscopy(EIS)was carried out on AM60 magnesium alloy specimens during 96 hour exposure periods into aerated 0.1mol/L NaCl,0.1mol/L Na2 SO4 and saturated Mg(0H)2 solutions.In the solutions containing C1-ions,the impedance spectroscopy takes on two capacitive loops in high frequency and middle frequency domain respedtively,while one inductive loop appears in first 36 hour immersion.The similar EIS behavior for AM60 in Na2 S04 solution had been observed,while the low frequency relaxation behavior is different.Comparing to the C1-ions,the S042-ions presented relatively weak corrosive ability.In the saturated Mg(OH)2 solution,due tO the anodic and cathodic reaction were restrained from the polarization curves by weak hydrolyzation of Mg(OH)2,the EIS behavior of AM60 differs from that in the other two aggressive ions solution.A relatively new method was applied to research the corrosion process with detail.Fractal dimension was calculated from the high frequency capacitive arc which was corresponding to the origin surface double electronic layer of AM60 magnesium in three kind solutions.The curves of fraetal dimension vs immersion time indicated that C1-ions presented the strongest corrosive attack,also shown the best self-repassivation behavior to recover the pits which.were produced by the existefiee of C1-ions.The SO42-ions attacked the surface of AM60,while the repassivation could be ignored.The increase of fractal dimension in Mg(OH)2 was mainly due to the adsorption of infusibility Mg(OH)2 on the surface increasing surface roughness.