Abstract:Electrochemical impedance spectroscopy(EIS)was carried out on AM60 magnesium alloy specimens during 96 hour exposure periods into aerated 0.1mol/L NaCl,0.1mol/L Na2 SO4 and saturated Mg(0H)2 solutions.In the solutions containing C1-ions,the impedance spectroscopy takes on two capacitive loops in high frequency and middle frequency domain respedtively,while one inductive loop appears in first 36 hour immersion.The similar EIS behavior for AM60 in Na2 S04 solution had been observed,while the low frequency relaxation behavior is different.Comparing to the C1-ions,the S042-ions presented relatively weak corrosive ability.In the saturated Mg(OH)2 solution,due tO the anodic and cathodic reaction were restrained from the polarization curves by weak hydrolyzation of Mg(OH)2,the EIS behavior of AM60 differs from that in the other two aggressive ions solution.A relatively new method was applied to research the corrosion process with detail.Fractal dimension was calculated from the high frequency capacitive arc which was corresponding to the origin surface double electronic layer of AM60 magnesium in three kind solutions.The curves of fraetal dimension vs immersion time indicated that C1-ions presented the strongest corrosive attack,also shown the best self-repassivation behavior to recover the pits which.were produced by the existefiee of C1-ions.The SO42-ions attacked the surface of AM60,while the repassivation could be ignored.The increase of fractal dimension in Mg(OH)2 was mainly due to the adsorption of infusibility Mg(OH)2 on the surface increasing surface roughness.

Electrochemical and Corrosion Behaviors of Pure Mg in Neutral 1.0% Nacl Solution

CORROSION BEHAVIOR OF PURE MAGNESIUM IN NEUTRAL 1.0mass. % NaCI SOLUTIONS

Corrosion behavior of magnesium and its alloy in NaCl solution

Electrochemical Noise Characteristics in Corrosion Process of Az91d Magnesium Alloy in Neutral Chloride Solution

Corrosion Behavior of Pure Mg Based on Generation/Collection and Feedback Modes of Scanning Electrochemical Microscopy

Electrochemical Impedance Fractal Study of AM60 Magnesium Alloy in Aggressive Solution

Corrosion behavior of anodized AZ91D magnesium alloy in NaCl aqueous solution

Understanding the Electrochemical Behavior of Bulk-Synthesized MgZn2 Intermetallic Compound in Aqueous NaCl Solutions As a Function of Ph

Electrochemical Behavior of ZE41 Magnesium Alloy under Simulated Atmospheric Corrosion

Determination of corrosion product film on pure Mg in Cl − environment using XPS etching

Localized Corrosion of Magnesium Alloys in NaCl Solutions Explored by Scanning Electrochemical Microscopy in Feedback Mode

Investigation of Az91d Magnesium Alloy Corrosion Behavior under Thin Electrolyte Layer Using Nondestructive Electrochemical Techniques

Electrochemical noise features of pure aluminum during pitting corrosion in neutral NaCl solution

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Electrochemical, TOF-SIMS and XPS Studies on the Corrosion Behavior of Q-phase in NaCl Solutions As a Function of Ph

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Gradient Textures Induce Micro-Galvanic Corrosion on Mg

Microstructure and Corrosion of Cast Magnesium Alloy ZK60 in NaCl Solution

Comparison on corrosion resistance and surface film of pure Mg and Mg−14Li alloy

A new look on the corrosion mechanism of magnesium: An EIS investigation at different pH

Electrochemical characterisation of a martensitic stainless steel in a neutral chloride solution