Abstract:In this study, through reasonable composition design, three elements of Zn, Mn and Ca, which are harmless to human body, were selected for alloying magnesium. The effects of ECAP treatment on the microstructure and corrosion properties of Mg-4Zn-1Mn-0Ca, Mg-4Zn-1Mn-0.2Ca and Mg-4Zn-0Mn-0.2Ca alloys were studied. The corrosion mechanism of Mg-Zn-Mn-Ca alloys with different components in Simulated. Body fluid (SBF) was analyzed by weight loss method and electrochemical test. The grains and the second phase were refined by Equal Angular Channel Pressing (ECAP). It was found that after 8 ECAP deformations, the microstructure of the alloy was refined and more uniform than that of the extruded alloy. The corrosion resistance of the Mg-Zn-Mn-Ca alloy after ECAP deformation in simulated body fluids was studied by electrochemical testing techniques, immersion experiments and observation of the microstructure and morphology of corrosion products. The relationship between microstructure characteristics, the behavior of the magnesium metal matrix and the properties of corrosion products was revealed. The results show that the microstructure of the alloy is refined and the corrosion resistance is improved with the increase in extrusion passes in the SBF solution. The corrosion resistance of magnesium alloy after 8 ECAP deformation is the best, showing small Icorr and large Rt. With the extension of the soaking time, the surface of the alloy will form a passivation film, which will protect the matrix and avoid further corrosion of the alloy. It is found that in SBF, the corrosion of the alloy surface is mainly pitting, which indicates that Ca2+, HCO3- and HPO42(-) in SBF can reduce the corrosion rate of magnesium alloy.

Localized Corrosion of Magnesium Alloys in NaCl Solutions Explored by Scanning Electrochemical Microscopy in Feedback Mode

In-situ AFM and quasi-in-situ studies for localized corrosion in Mg-9Al-1Fe-(Gd) alloys under 3.5 wt.% NaCl environment

Corrosion Behavior of Pure Mg Based on Generation/Collection and Feedback Modes of Scanning Electrochemical Microscopy

An In-Situ Degradation Behavior Study of Mao Coating on Az91d Magnesium Alloy in Aqueous Solutions by Secm

Local galvanic corrosion analysis on cast Mg-Ca binary alloy using scanning Kelvin probe force microscopy

Multi-scale study on the electrochemical behavior and corrosion mechanism of 5083 aluminum alloy with different microstructures in a NaCl environment

Corrosion behavior of magnesium and its alloy in NaCl solution

The Effects of ECAP, Mn and Ca Elements on the Microstructure and Corrosion Properties of Magnesium Alloys Were Investigated

Study of the Corrosion Product Films Formed on the Surface of Mg–xZn Alloys in NaCl Solution

Electrochemical Corrosion Characterization of As-Cast Mg-7Li Alloy

Effect of Chloride Ion Concentration on Electrochemical Behavior and Corrosion Product of Am60 Magnesium Alloy in Aqueous Solutions

Possibilities and Limitations of Scanning Electrochemical Microscopy of Mg and Mg Alloys

Electrochemical and Corrosion Behaviors of Pure Mg in Neutral 1.0% Nacl Solution

Formation Mechanisms of Product Film on High Corrosion Resistant EW75 Mg Alloy: the Effect of Corrosive Media

Effects of Corrosive Media on the Localized Corrosion Forms of Mg-3Zn Alloy

Use of Amperometric and Potentiometric Probes in Scanning Electrochemical Microscopy for the Spatially-Resolved Monitoring of Severe Localized Corrosion Sites on Aluminum Alloy 2098-T351

CORROSION BEHAVIOR OF PURE MAGNESIUM IN NEUTRAL 1.0mass. % NaCI SOLUTIONS

Surface Characterisation Of Rapidly Solidified Mg-Based Alloys Immersed In 3%Nacl Solution

Corrosion Characterization of Mg–8Li Alloy in NaCl Solution

Electrochemical Behavior of ZE41 Magnesium Alloy under Simulated Atmospheric Corrosion

High-frequency induction for surface alloying of magnesium alloy ZM5 and its corrosion behavior