Abstract:Aluminum alloys are extensively used to manufacture mechanical components. However, when exposed to alkaline environments, like lubricants, refrigerants, or detergents, they can be corroded, reducing their durability. For this reason, the aim of this study is to investigate the influence of aggressive alkaline solutions (i.e., pH and presence of chlorides) on the corrosion resistance of three aluminum alloys (AA 5083-H111, AA 6082-T6, and AA 7075-T6) with and without anodizing treatments. Open circuit potential (EOCP) and anodic polarization measurements were carried out and typical corrosion parameters such as corrosion current density (icor) and corrosion rate (CR) were determined. Morphology of the corrosion attack and samples microstructure were investigated by scanning electron microscope. Results show that corrosion behavior of the three investigated alloys is influenced by (i) the aggressiveness of the testing environments; (ii) the thickness of the anodizing treatment; (iii) the alloy chemical composition; (iv) the distribution of intermetallic phases in the aluminum matrix. Moreover, three galvanic series have been built also testing other metallic alloys commonly used in mechanical applications, i.e., carbon steel (C40), stainless-steel (AISI 304), and Cu-based alloys (Cu-Ni alloy and CW 617 N, respectively). Results clearly indicate that galvanic series play a fundamental role when it is necessary to select an alloy for a specific environment, highlighting the thermodynamic conditions for corrosion occurrence. On the other hand, kinetic measurements and microstructural studies carried out on the three aluminum alloys stress the importance of the surface treatments and relevant thickness as well as the effect of metal exposure. Future work will involve the study of other surface treatments on aluminum alloys and the evaluation of their corrosion behavior in acidic environments.

Synergistic Effects of Corrosion and Slow Strain Rate Loading on the Mechanical and Electrochemical Response of an Aluminium Alloy

Interaction of Mechanical and Electrochemical Factors During Corrosion-Fatigue of Fe-26cr-1mo Stainless-Steel in 1m H2so4 Solution

The Effect of Applied Tensile Stress on the Exfoliation Corrosion of 7075‐T6 Alloy

Multiaxial Fatigue of 6061-T6 Aluminum Alloy under Corrosive Environment

Microstructure Evolution and the Resulted Influence on Localized Corrosion in Al-Zn-Mg-Cu Alloy during Non-Isothermal Ageing

INFLUENCE OF TENSILE STRESS ON EXFOLIATION CORROSION AND ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY OF 7075al - ALLOY

Corrosion Fatigue Behaviors of Two Biomedical Mg Alloys-Az91d and We43-In Simulated Body Fluid

Corrosion Behavior of Aluminum Alloys in Different Alkaline Environments: Effect of Alloying Elements and Anodization Treatments

In Situ Electrochemical Monitoring of the Crevice Corrosion Process of the 7075-T651 Aluminium Alloy in Acidic NaCl and NaNO3 Solution

Effect of solution pH on stress corrosion and electrochemical behaviour of aluminum alloy with micro-arc oxidation coating

Linking the effect of localised pitting corrosion with mechanical integrity of a rare earth magnesium alloy for implant use

Synergistic Effect of Environmental Media and Stress on the Fatigue Fracture Behaviour of Aluminium Alloys

Environment-induced Fatigue Cracking Behavior of Aluminum Alloys and Modification Methods

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling

In Situ Atomic Force Microscopy Observations of the Corrosion Behavior of Aluminum‐Copper Alloys

Influence of Interfacial Stress Produced by MAO on Electrochemical Corrosion and Stress Corrosion Cracking Behavior in 7075 Aluminum Alloy

Fatigue damage evolution and failure of pre‐corroded aluminum alloy 7075‐T651 under air and corrosion environments

High Rate Mechanical Characterization of Sensitized 5083-H131 Aluminum Alloy

Stress corrosion behavior and microstructure analysis of Al-Zn-Mg-Cu alloys friction stir welded joints under different aging conditions

Corrosion Fatigue Behavior of Fastening Hole Structure and Virtual Crack Propagation Tests

Corrosion property of Al alloys subjected to surface severe plastic deformation: a review