Abstract:Medical bone implant magnesium (Mg) alloys are subjected to both corrosive environments and complex loads in the human body. The increasing number of hyperglycemic and diabetic patients in recent years has brought new challenges to the fatigue performance of Mg alloys. Therefore, it is significant to study the corrosion fatigue (CF) behavior of medical Mg alloys in glucose-containing simulated body fluids for their clinical applications. Herein, the corrosion and fatigue properties of extruded Mg-Zn-Zr-Nd alloy in Hank's balanced salt solution (HBSS) containing different concentrations (1 g/L and 3 g/L) of glucose were investigated. The average grain size of the alloy is about 5 μm, which provides excellent overall mechanical properties. The conditional fatigue strength of the alloy was 127 MPa in air and 88 MPa and 70 MPa in HBSS containing 1 g/L glucose and 3 g/L glucose, respectively. Fatigue crack initiation points for alloys in air are oxide inclusions and in solution are corrosion pits. The corrosion rate of the alloy is high at the beginning, and decreases as the surface corrosion product layer thickens with the increase of immersion time. The corrosion products of the alloy are mainly Mg(OH) 2 , MgO and a small amount of Ca-P compounds. The electrochemical results indicated that the corrosion rate of the alloys gradually decreased with increasing immersion time, but the corrosion tendency of the alloy was greater in HBSS containing 3 g/L glucose. On the one hand, glucose accelerates the corrosion process by adsorbing large amounts of aggressive Cl − ions. On the other hand, glucose will be oxidized to form gluconic acid, and then reacts with Mg(OH) 2 and MgO to form Mg gluconate, which destroys the corrosion product film and leads to the aggravation of corrosion and the accumulation of fatigue damage.

Corrosion Fatigue Behaviors of Two Biomedical Mg Alloys-Az91d and We43-In Simulated Body Fluid

Recent progress in fatigue behavior of Mg alloys in air and aqueous media: A review

Biodegradation of Az31 and We43 Magnesium Alloys in Simulated Body Fluid

Fatigue behaviors of HP-Mg, Mg-Ca and Mg-Zn-Ca biodegradable metals in air and simulated body fluid

Corrosion behavior of biomedical AZ91 magnesium alloy in simulated body fluids

Effects of Inorganic Ions, Organic Particles, Blood Cells, and Cyclic Loading on in Vitro Corrosion of Mg Al Alloys

On the Corrosion Fatigue of Magnesium Alloys Aimed at Biomedical Applications: New Insights from the Influence of Testing Frequency and Surface Modification of the Alloy ZK60

Stress corrosion cracking and corrosion fatigue characterisation of MgZn1Ca0.3 (ZX10) in a simulated physiological environment

Research Progress on Corrosion Fatigue Behavior of Biomedical Degradable Magnesium-Based Alloys

Influence of load frequency and corrosive environments on fatigue behavior of as-extruded Mg–Zn–Zr–Nd alloy

Fatigue and Corrosion Fatigue Properties of Mg–Zn–Zr–Nd Alloys in Glucose-Containing Simulated Body Fluids

Corrosion Products on Biomedical Magnesium Alloy Soaked in Simulated Body Fluids

Electrochemical Behavior Al[sub 2]o[sub 3]∕al Coated Surgical AZ91 Magnesium Alloy in Simulated Body Fluids

In vitro degradation and biocompatibility of WE43, ZK60, and AZ91 biodegradable magnesium alloys

A Numerical Corrosion-Fatigue Model for Biodegradable Mg Alloy Stents.

In vitro corrosion behavior of the extruded Mg–4Zn–1Mn alloy in different physiological solutions for biomedical applications

In vitro bio-corrosion behaviors of biodegradable AZ31B magnesium alloy under static stresses of different forms and magnitudes

Impact of Corrosion in Simulated Body Fluid on Fatigue Characteristics of 3D-Printed Polylactic Acid-Coated AM60 Magnesium Alloys

Simulated Body Fluid-Assisted Stress Corrosion Cracking of a Rapidly Solidified Magnesium Alloy RS66

Corrosion behavior and mechanical properties of extruded low-alloyed Mg−0.5Bi−0.5Y−0.2Zn alloy

Corrosion Behavior of Zrn/Zr Coated Biomedical Az91 Magnesium Alloy