Impact of Corrosion in Simulated Body Fluid on Fatigue Characteristics of 3D-Printed Polylactic Acid-Coated AM60 Magnesium Alloys

Seyed Ali Ashraf Talesh,Mohammad Azadi

DOI: https://doi.org/10.3390/surfaces7010007

2024-02-05

Surfaces

Abstract:In this research, the pure fatigue behaviors of AM60 magnesium alloy with polylactic acid (PLA) coating (PF-AM60-PLA) and the corrosion fatigue behaviors of magnesium alloy with PLA coating (CF-AM60-PLA) were evaluated. Polymer coating was made by fused deposition modeling (FDM) with a 3D printer and attached to standard fatigue test specimens with glue. Then, after 27 days of immersion in the simulated body fluid (SBF), the high-cycle bending fatigue test was performed on samples. Due to corrosion, the weight of the specimens was reduced by an average of 35%. The corrosion rate decreased in the first 7 days and then increased. PF samples with a coating had an average 49% increase in fatigue lifetime. Regarding the CF samples, despite the use of a 10-times stronger solution, the fatigue lifetime of these samples decreased by only 35%. The field-emission scanning electron microscopy (FESEM) results also showed cleavage plates and striations. In addition, the separation of the glue from the coating and Mg was observed. Corrosion products, in addition to microcracks and holes, were seen on the fracture surface of CF specimens, which caused the stress concentration and the crack initiation. Holes caused by the release of gases were also observed in polymer coatings, which were fabricated by 3D printing.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to evaluate the effect of corrosion on the fatigue properties of 3D - printed polylactic acid (PLA) - coated AM60 magnesium alloy. Specifically, the research aims to:

1. **Compare pure fatigue behavior and corrosion - fatigue behavior**: The researchers evaluated the fatigue properties of PLA - coated AM60 magnesium alloy without corrosion treatment (PF - AM60 - PLA) and PLA - coated AM60 magnesium alloy after simulated body fluid (SBF) corrosion (CF - AM60 - PLA) respectively.

2. **Explore the effect of corrosion on fatigue life**: By conducting high - cycle bending fatigue tests after soaking in simulated body fluid for 27 days, the researchers hope to understand how corrosion affects the fatigue life of the material. The results show that corrosion causes an average 35% reduction in sample weight, and the corrosion rate decreases in the first 7 days and then increases.

3. **Analyze the role of the coating**: The researchers also explored the effect of the PLA coating on the fatigue life of the magnesium alloy. The results indicate that the fatigue life of PF samples with coating increased by an average of 49%. Although a 10 - fold concentration of the corrosion solution was used, the fatigue life of CF samples decreased by only 35%.

4. **Microstructural analysis**: Through field - emission scanning electron microscopy (FESEM) observations, the researchers found cracks, delamination, and bonding failure between the coating and the substrate. These microstructural changes are helpful for understanding the damage mechanisms during corrosion and fatigue processes.

### Formula representation

The corrosion rate can be calculated by the following formula:

\[
\text{Corrosion rate}=\frac{KW}{AtD}
\]

where:
- \(A\) is the area of the sample exposed to the environment (\(\text{cm}^2\))
- \(W\) is the weight loss (g)
- \(D\) is the material density (\(\text{g/cm}^3\))
- \(t\) is the exposure time (hours)
- \(K = 3.45\times10^6\)

Through these research contents, the paper aims to provide a deeper understanding of magnesium alloy materials in biomedical applications, especially in applications such as implants and stents, on how to improve the corrosion resistance and fatigue life of materials through surface modification techniques.