Abstract:Nitrogen-alloyed austenitic stainless steel QN1803 (2.0%Ni-3.5%Ni) has been developed to replace the conventional 304 stainless steel (8%Ni). Both the microstructure and the corrosion resistance of both types of stainless steels in the annealed state have been extensively studied, whereas those in the cold strained state have not been studied sufficiently. The aforementioned stainless steels often undergo cold forming processes during industrial applications, such as straightening, leveling, and bending, etc., which may lead to the changes of microstructure and corrosion resistances as well as the performance. In this study, the tensile tests were performed with different tensile strains for both nitrogenalloyed QN1803 and the conventional 304 stainless steels. The microstructure and strengthening, as well as the toughening mechanisms were investigated using EBSD, XRD, and TEM. The corrosion resistance and its mechanism under different tensile strains were evaluated and analyzed via electrochemical workstation, acid corrosion tests, OM, and SEM. Notably, the microstructures of both QN1803 and 304 stainless steels are changed from dislocation plugging to a' martensite with the increase in tensile strain. The yield strength of QN1803 stainless steel is 26% higher, while its elongation is 6.6% lower than that of 304 stainless steels, respectively. This could be attributed to both the higher nitrogen content and the lower transition temperature of 50% martensite induced by 30% strain (M-d30) for QN1803 stainless steel as compared with that for 304 stainless steel. As a result, the volume fraction of the strain-induced martensite for QN1803 stainless steel under tensile strain is lower, leading to the lower toughening effect than that of 304 stainless steel. Interestingly, the experiments show that the tensile strain has a minor effect on the intergranular corrosion whereas noticeably negative effect on both the pitting and the sulfuric acid corrosion resistances of both stainless steels. Not surprisingly, 304 stainless steel undergoes a more remarkable decrease in both the pitting and the sulfuric acid corrosion resistances with the increase in tensile strain as compared with QN1803 stainless steel. This could be well understood since martensite could lead to the destruction or deterioration of the passive film on the stainless steel surface, producing an unstable dissolution-generation state during corrosion, thus reducing the corrosion resistance after tensile deformation. In conclusion, the yield strength is enhanced, ductility is slightly impaired, and both the pitting and the sulfuric acid corrosion resistances under tensile deformation are improved by nitrogen alloying. Based on these technical advantages, together with the nickel saving effect, QN1803 stainless steel has been applied in various industrial areas, such as building, construction, and home appliance, etc.

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: understanding electrochemical corrosion with tensile stress coupling

Corrosion of high-strength steel in 3.5% NaCl solution under hydrostatic pressure: Initial corrosion with tensile stress coupling

Anomalous Evolution of Corrosion Behaviour of Warm-Rolled Type 304 Austenitic Stainless Steel

Electrochemical corrosion behavior of high strength steel in simulated deep-sea environment under different hydrostatic pressure

A Primary Study of the Effect of Hydrostatic Pressure on Stress Corrosion Cracking of Ti-6Al-4V Alloy in 3.5% NaCl Solution

Effect of hydrostatic pressure on galvanic corrosion of low-alloy steel in simulated deep-sea environments

Effect of hydrostatic pressure on the galvanic corrosion of 90/10 Cu-Ni alloy coupled to Ti6Al4V alloy

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Corrosion Of High-Strength Steel Wires Under Tensile Stress

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Effect of Tensile Deformation on Microstructure and Corrosion Resistance of High Nitrogen Austenitic Stainless Steels

STRESS CORROSION CRACKING BEHAVIOR OF A NEW KIND OF ULTRAHIGH STRENGTH STEEL Cr12Ni4Mo2Co14 IN ACID ENVIRONMENT

Effect of Hydrogen on Plastic Deformation Near Crack-tip of A537 Steel in 3.5%nacl Solution

Galvanic Corrosion Study between Tensile-Stressed and Non-Stressed Carbon Steels in Simulated Concrete Pore Solution

Effect of Organizational Evolution on the Stress Corrosion Cracking of the Cr-Co-Ni-Mo Series of Ultra-High Strength Stainless Steel

Corrosion Behavior of Ultrafine-Grained CoCrFeMnNi High-Entropy Alloys Fabricated by High-Pressure Torsion

Effect of Dissolved Oxygen on Pitting Corrosion Behavior of Low-Alloy Steel under Hydrostatic Pressure

Study on the mechanism of hydrostatic pressure promoting electrochemical corrosion of pure iron in 3.5% NaCl solution

Threshold stress intensity of hydrogen-induced cracking and stress corrosion cracking of high strength steel

Investigations on corrosion behavior of 316LN and 316L austenitic stainless steel under corrosion-deformation interactions