Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Effect of Hydrogen on Plastic Deformation Near Crack-tip of A537 Steel in 3.5%nacl Solution

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Effects of Crack Position on Fatigue Life of Large Seamless Storage Vessels Made of 4130X for Hydrogen Refueling Station

Molecular dynamics study on the effect of hydrogen on the plastic behavior of α-Fe crack tip

Crack Growth Retardation of Single Overload for A537 Steel in a 3.5% NaCl Solution under Cathodic Potential and Free Corrosion Condition

Hydrogen Effect on the Fatigue Crack Growth in Austenitic Stainless Steel Investigated by a New Method Based on Nanohardness Distribution

Special Fatigue Fracture Behavior of Nanocrystalline Metals under Hydrogen Conditions

Influences of Solution Hydrogen on the Fatigue Crack Propagation Lives of TA15 Alloys Electron Beam Welded Joints

Effect of Hydrogen Charging on the Stress Corrosion Cracking Behavior of X70 Steel in Simulated Deep Seawater Environment

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

Hydrogen diffusion behavior within microstructures near crack tip: A crystal plasticity study

Effects of Electrochemical Hydrogen Charging Parameters on the Mechanical Behaviors of High-Strength Steel

Threshold stress intensity of hydrogen-induced cracking and stress corrosion cracking of high strength steel

Effects of Hydrogen Pressure on Hydrogen-Assisted Fatigue Crack Growth of Cr-Mo Steel

Hydrogen-Assisted Brittle Fracture Behavior of Low Alloy 30CrMo Steel Based on the Combination of Experimental and Numerical Analyses

Effects of External Hydrogen on Hydrogen Transportation and Distribution Around the Fatigue Crack Tip in Type 304 Stainless Steel

Effects of hydrogen on the fracture toughness of X80 steel base metal and girth weld under strong cathodic current with in-situ hydrogen charging

Effects of hydrogen and load frequency on the fatigue crack propagation behavior of selective laser melted Inconel 718 alloy

Hydrogen-Enhanced Fatigue Crack Growth in a Single-Edge Notched Tensile Specimen Under In-Situ Hydrogen Charging Inside an Environmental Scanning Electron Microscope

Analysis of fatigue fracture with cyclic overloading for A537 steel in 3.5%NaCl solution at an applied cathodic potential

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel