Effect of Fe/Mn content on mechanical and corrosion properties of 90/10 copper–nickel alloy
Guosen Shao,Yuhang Gao,Jiayan Wu,Ping Liu,Ke Zhang,Wei Li,Fengcang Ma,Honglei Zhou,Xiaohong Chen
DOI: https://doi.org/10.1002/maco.202112748
2022-02-10
Materials and Corrosion
Abstract:The effect of Fe/Mn content on the metallographic structure, mechanical properties, and corrosion resistance of 90/10 copper–nickel alloy using electrochemical methods, scanning electron microscope, energy dispersive spectroscopy, X‐ray photoelectron spectroscopy, Tafel experiments, and electrochemical impedance spectroscopy measurements were investigated in this paper. The experimental results indicated that the tensile strength of the alloys increases from 326 to 347 MPa with the change of Fe/Mn content, the yield strength of 90/10 copper–nickel alloys is approximately 150 MPa, and the elongation of the alloys was reduced from 51% to 37%. Moreover, as corrosion proceeds, the corrosion product film was mainly composed of Cu2O, Cu2(OH)3Cl. In addition, the Cu–10Ni alloy with Fe/Mn content of 1.69/0.69 has good corrosion resistance properties. The effect of Fe/Mn content on the metallographic structure, mechanical properties, and corrosion resistance of 90/10 copper–nickel alloy using electrochemical methods, scanning electron microscope, energy dispersive spectroscopy, X‐ray photoelectron spectroscopy, Tafel experiments, and electrochemical impedance spectroscopy measurements were investigated. The 90/10 copper–nickel alloy with an Fe content of 1.69% had the highest Ecorr values, making it more resistant to corrosion than other 90/10 copper–nickel alloys.