Abstract:This paper deals with a systematic investigation on the synthesis of aluminium oxide starting from mono hydroxy aluminium oxide (boehmite, (AlOOH)) which in turn is synthesized from aluminium nitrate. Boehmite on heating forms γ, transitional alumina and α-alumina phases in the temperature range 400–600, 800–1050 and 1050–1100°C respectively. Calculation from XRD, using Scherer equation shows that γ-alumina has crystallite size in the range 5–10 nm, while δ and θ-alumina are in the range 10–20 nm and α-alumina is about ∼33 nm. The textural features of aqueous sol-gel boehmite samples calcined at various temperatures were analyzed by specific surface area measurements and adsorption isotherm features. Maximum specific surface area of 266 m2/g is observed for the precursor calcined at 400°C and a minimum of 5 m2/g at 1100°C. Total pore volume is maximum for the precursor calcined at 600°C (0.2653 cm3/g). Average pore size ranges from ∼3 nm (400°C) to ∼11 nm (1100°C). The adsorption isotherms also show a change from Type IV to Type II with increase in temperature showing difference in surface properties. The information from t-plots, pore size distribution and cumulative pore volume data also indicates differences in porosity features of boehmite on calcination. The adsorption isotherm and pore size distribution analysis show maximum microporosity at 400°C, while maximum mesoporosity is observed at 600°C. At higher temperatures, porosity decreases, even though small fraction of pores in the mesopore range is still retained. At 1100°C, there is structural transformation from transitional to α-alumina, with very low specific surface area ∼5 m2/g and pores in the size range of 11 nm. The various data presented in this study will be useful in the synthesis of alumina with tailor made properties.

Reparation and characterization of transparent boehmite (gamma-AlOOH) sol

Preparation and Characterization of Transparent Boehmite (γ-AlOOH) Sol

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Adsorption Isotherm and Pore Characteristics of Nano Alumina Derived from Sol-Gel Boehmite

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

Preparation and Optical Properties of Transparent Alumina Film by the Sol-gel Method

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Preparation of Pseudo-Boehmite and Gamma-Al2o3 by Polyaluminum Chloride Ii -Surfactant Influences

Boehmite Preparation via Alditols-Interacting Transformation of Metastable Intermediates in Al–H2O Reaction Crystallization

Preparation and Characterization of gamma-Al2O3 Nanocrystals by Hydrothermal Assisted Sol-gel Method

Morphological Characterization of γ-Al 2 O 3 Membranes Fabricated from Ammonium Aluminum Sulphate

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

A new route to synthesis of γ-alumina nanorods

Preparation and Characterization of Nanocrystalline Gamma-Al2o3 by Sol-Gel Process

Hydrothermal stability of gamma-Al 2 O 3 supports varied with crystal plane orientation of pseudo-boehmite precursor

Synthesis, Characterization and Catalytic Applications of Mesoporous Γ-Alumina from Boehmite Sol

Effects of synthetic conditions on the textural structure of pseudo-boehmite

Porosity evaluation and positron annihilation study of mesoporous aluminum oxy-hydroxide ceramics

Reactive Crystallization Kinetics Study of Boehmite in Ammonia Solution by Adding Ammonium Aluminum Sulfate

The Fabrication of the Hydrous Alumina Powders by the Sol-Gel Method