Preparation and Characterization of Alumina-Zirconia Nanoparticles
Zhao Jihua,Zhang Ying,Xie Xiaoyun,Hao Xiaojuan,Shen Weiguo,An Xueqin
DOI: https://doi.org/10.3321/j.issn:0455-2059.2005.04.013
2005-01-01
Abstract:Al2O3-ZrO2 nanoparticles were obtained in the microemulsion of water/Triton X-100/n-butanol /cyclohexane. A variety of conditions for the preparation of Al(OH)3-Zr(OH)4 nanoparticles were investigated. The sizes of the nanoparticles were measured by dynamic light scattering and he results showed that the reaction temperature, the mole ratio of water to surfactant (Rw), and the concentration of the reactants are the predominant factors in controlling the particle size and distribution of Al(OH)3-Zr(OH)4. The phase transformation, structure and morphology of Al2O3- ZrO2 nanoparticles were characterized by TEM, XRD, IR and TG, respectively. The results show that the nanoparticles calcined in vacuum at 60℃ are amorphous, and t-ZrO2 appears as a predominant phase upon calcining the nanoparticles at 500℃; further heating the nanoparticles at 1200℃ leads to t-ZrO2, m-ZrO2 and α-Al2O3. TEM show that the average particle size is 5 nm and 200 nm at 500, 1200℃, respectively.