Abstract:Si3N4 ceramics with improved thermal conductivity and mechanical properties were prepared by carbothermal reduction and two‐step sintering. The addition of 2 wt% C led to the development of an intergranular phase YNSiO2 with reduced oxygen content. Notably, setting the pre‐sintering temperature at 1450°C promoted the formation of a rough bimodal morphology within the Si3N4 ceramics. Furthermore, an extended holding period at 1850°C resulted in additional grain growth and the elimination of intergranular phases. The Si3N4 specimens produced at 1450°C for 3 h followed by 1850°C for 8 h, incorporating 2 wt% C, exhibited a notable continuity between Si3N4 grains. The thickness of the grain boundary layer was only about 1 nm, and the N/O atomic ratio of the intergranular phase was measured to be 0.42. Consequently, the resulting thermal conductivity, flexural strength, and fracture toughness of Si3N4 specimens were found to be 101 W·m−1·K−1, 712 ± 29 MPa, and 7.7 ± 0.2 MPa·m1/2, respectively. Compared with samples without C additive and directly sintered at 1850°C for 8 h, the Si3N4 specimens produced in this work showed a significant increase of more than 50% in thermal conductivity and about 17% in fracture toughness.

Precisely Controlled Carbothermal Synthesis of Spherical Β-Si3n4 Granules

Carbothermal Synthesis Of Micron-Sized Beta-Si3n4 With Tailored Morphology

Synthesis and Growth Mechanism of Single Crystal Β‐si3n4 Particles with a Quasi‐spherical Morphology

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Synthesis and Growth Mechanism of Approximate Spherical Β‐si3n4 Particles Via Carbothermal Reduction‐nitridation Method

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

In‐situ combustion synthesis of spherical Si@Si <sub>3</sub> N <sub>4</sub> granules

In‐situ combustion synthesis of spherical Si@Si3N4 granules

Synthesis of well-dispersed β-Si3N4 with equiaxed structures using carbothermal reduction–nitridation method

In situ combustion synthesis of spherical Si@Si<sub>3</sub>N<sub>4</sub> granules

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis of Well-Dispersed Columnar Si 3 N 4 Using Carbothermal Reduction–nitridation Method

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Carbothermally prepared nanophase SiC/ Si3N4 composite powders and densified parts

Preparation of β-Si3N4 Single Crystal Particles

Preparation of the Rod-Like Β-Si3n4 Particles Favoring the Self-Reinforcing Si3N4 Ceramics

Fabrication of Spherical Thermal-Conductive Silicon Nitride Powder

Carbothermal Synthesis of Micro-Scale Spherical Aln Granules with Caf2 Additive

Phase-controlled Synthesis of Nickel Silicide Nanostructures

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering