Abstract:Due to their special appearance, spherical α‐Al2O3 nanoparticles play an important role for obtaining high performance structural and functional ceramics. However, there are still problems such as easily agglomerates to form worm‐like structures at high temperatures and difficult availability of spherical nanoparticles. In this study, spherical α‐Al2O3 nanoparticles with high dispersion were prepared by combination of microwave hydrothermal method and addition of nano‐Al particles as seeds. Firstly, spherical amorphous alumina precursors were synthetized by microwave hydrothermal method at 100°C for 30 min using Al2(SO4)3∙18H2O, Al(NO3)3∙9H2O and urea as raw materials, and then, spherical α‐Al2O3 nanoparticles with diameter of about 66 nm were acquired after calcined the precursor at 1050°C for 90 min by adding nano‐Al seeds, which reduced the calcination temperature by 50°C and holding time by 30 min compared to that without seeds. Kinetic analysis shows that 5 wt.% nano‐Al seeds can reduce the activation energy of crystalline transition of γ‐Al2O3 to α‐Al2O3 from 516.51 kJ/mol to 474.37 kJ/mol. Moreover, the microscopic mechanism of nano‐Al particles as seeds was investigated. The characterizations of sintering properties show that spherical α‐Al2O3 nanoparticles facilitate the acquisition of uniform microstructure for resulting ceramic and the fracture modes include both intergranular and transgranular fracture.This article is protected by copyright. All rights reserved

Carbothermal Synthesis of Micro-Scale Spherical Aln Granules with Caf2 Additive

Carbothermal Synthesis of Spherical AlN Granules: Effects of Synthesis Parameters and Y2O3 Additive

Preparation of Spherical AlN Granules Directly by Carbothermal Reduction–Nitridation Method

Carbothermal Synthesis of Spherical AlN Fillers

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Facile synthesis of monodisperse aluminum nitride microspheres

Carbothermal Synthesis Of Micron-Sized Beta-Si3n4 With Tailored Morphology

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

Precisely Controlled Carbothermal Synthesis of Spherical Β-Si3n4 Granules

AlN Powder Synthesis by Sodium Fluoride-Assisted Carbothermal Combustion

Synthesis of Ultrafine AlN Powders in an Al-OC-N System

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis of Nano-Size AlN Powders by Carbothermal Reduction from Plasma-Assisted Ball Milling Precursor

Synthesis of aluminum nitride fibres from aluminum silicate fibres by carbothermal reduction method

Promoting Effect of Silicon Particles on Gas-Diffusion-reaction System: In-situ Synthesis of AlN in Al-Si Materials

Synthesis of Meso/macroporous Aluminum Nitrides Via Aluminum Alloy Ceramization

AlN ceramics synthesized by carbothermal reduction of mechanical activated Al2O3

Gas‐Phase and Solid‐State Simultaneous Mechanism for Two‐Step Carbothermal AlON Formation

Preparation of AlN Powder of Low Oxygen Content Via Carbothermal Reduction and Nitridation by Active Gas Exchange Technique

Preparation of spherical α‐Al 2 O 3 nanoparticles by microwave hydrothermal synthesis and addition of nano‐Al seeds