Abstract:Aluminium nitride (AlN) is an important technical ceramic with outstanding strength and thermal conductivity that has important applications for advanced heat sink materials and as a reinforcement for metal-based composites. In this study, we report a novel, straightforward and low-cost method to prepare AlN powder using a vacuum tube furnace for the direct nitridation of loose aluminium powder at low temperatures (down to 500 ∘C) under flowing high-purity nitrogen. Small amounts of magnesium powder (1 wt.%), combined with aluminium, promote nitridation. Here, we characterise the effects of time (up to 12 h) and temperature (490 to 560 ∘C) on nitridation with the aim to establish an effective regimen for the controlled synthesis of an aluminium nitride reinforcement powder for the production of metal matrix composites. The extent of nitridation and the morphology of the reaction products were assessed using scanning electron microscopy and X-ray diffraction analyses. AlN was detected for all nitriding temperatures ≥ 500 ∘C, with the highest yields of 80% to 85% obtained at 530 ∘C for times ≥ 1 h. At this temperature, nitridation proceeded rapidly, and there was extensive agglomeration of the reaction products making it difficult to reprocess into powder. At lower temperatures around 510 ∘C, a relatively high proportion of AlN was attained (>73% after 6 h) while retaining excellent friability so that it could be manually reprocessed to powder. The synthesised reinforcement consisted of micro- or nano-crystalline AlN comingled with metallic aluminium. The ratio of AlN and metallic aluminium can be readily controlled by varying the nitriding temperature. This provides a flexible and accessible method for the production of AlN-reinforcement powders suited to the production of metal matrix composites.

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Synthesis of Aluminum Nitride by Nitridation of Γ-Al2o3 Nanoparticles in Flowing Ammonia

Facile synthesis of monodisperse aluminum nitride microspheres

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Impacts of Temperature and Time on Direct Nitridation of Aluminium Powders for Preparation of AlN Reinforcement

Synthesis of Ultrafine AlN Powders in an Al-OC-N System

Mechanism of carbothermal synthesis of aluminium nitride

Synthesis of Aluminium Nitride by Direct Nitridation of Molten Al-Mg-Si Alloys

Synthesis of aluminum nitride fibres from aluminum silicate fibres by carbothermal reduction method

Preparation of Spherical AlN Granules Directly by Carbothermal Reduction–Nitridation Method

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Carbothermal Reduction Nitridation of Fly Ash, Diatomite and Raw Illite: Formation of Nitride Powders with Different Morphology and Photoluminescence Properties

A novel method for preparation of aluminum nitride powders in air

Thermodynamic and kinetic analyses of vacuum synthesis of AlN by the alumina carbothermal reduction nitridation method

Synthesis of AlN particles via direct nitridation in a drop tube furnace

High purity and good dispersity AlN nanoparticles synthesized by an arc discharge with assistance of direct nitridation

SYNTHESIS OF ALUMINUM NITRIDE POWDER BY IN SITU REACTION

Evolution of Aluminum Nitride Nanostructures from Nanoflower to Thin Film on Silicon Substrate by Direct Nitridation of Aluminum Precursor

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders