Abstract:We propose a facile and continuous direct nitridation method for synthesizing fine aluminum nitride (AlN) particles using a drop tube furnace. Aerosolized Al powder as the raw material was continuously supplied through the top of the furnace together with N2 as a carrier gas. Once in the furnace, the Al powder reacted with the N2 to form AlN. A particular advantage of this process is that it allows the continuous synthesis of fine AlN particles. In this study, either a mullite (Al2O3–SiO2) or an alumina tube was used to fabricate the furnace, and the products were collected in a crucible placed at the bottom. Upon heating the mullite tube from 1200 to 1400°C, AlN was formed once the temperature exceeded 1250°C, and its product content increased with temperature. When the flow rate of the N2 carrier gas was decreased from 4 to 2 L min−1, the amount of AlN formed increased due to the increased residence time in the reactor. The morphology of the particles obtained was radially aligned nanofibers with droplets on the tips of the fibers. Transmission electron microscopy revealed that the Si in the mullite tube reacted with Al to form eutectic Al–Si droplets on the Al surface, in which these droplets acted as a catalyst of vapor–liquid–solid AlN fiber growth. When the alumina tube was used (1800°C), nitridation of Al was enhanced and radially aligned AlN nanofibers with no droplets on the tips were collected, mainly in a filter at the exhaust port. These AlN nanofibers are thought to form via vapor–solid growth and are easily carried along with the N2 gas flow, resulting in their deposition on the filter. The products collected in the crucible contained coarse Al particles, which are formed via Al particle agglomeration and coarsening through melting.

Evolution of Aluminum Nitride Nanostructures from Nanoflower to Thin Film on Silicon Substrate by Direct Nitridation of Aluminum Precursor

Vapor-Solid Growth And Characterization Of Aluminum Nitride Nanocones

Synthesis and field emission properties of aluminum nitride nanocones

Morphology Evolution, Growth Mechanism and Optical Properties of AlN Nanostructures

Vertically aligned one-dimensional AlN nanostructures on conductive substrates: Synthesis and field emission

Catalyst-Free Synthesis, Morphology Evolution and Optical Property of One-Dimensional Aluminum Nitride Nanostructure Arrays

In-Situ Chloride-Generated Route to Different AlN Nanostructures on Si Substrate

Controllable Synthesis of One-Dimensional Aluminum Nitride Nanostructures Through Vapor-Solid Epitaxial Growth

0001] oriented aluminum nitride one-dimensional nanostructures: synthesis, structure evolution, and electrical properties

Facile synthesis of monodisperse aluminum nitride microspheres

Optimization of growth parameters of AlN thin films and investigation of electrical and electroluminescence characteristics from Au/i-AlN/n-GaN UV light-emitting diode

Low-temperature Synthesis of AlN Films Through Electron Cyclotron Resonance Plasma-Aided Reactive Pulsed Laser Deposition

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Sublimation Growth of Aluminum Nitride on Silicon Carbide Substrate with Aluminum Nitride–silicon Carbide Alloy Transition Layer

Preparing aluminum nitride thin film by atomic layer deposition

Synthesis of Aluminum Nitride by Nitridation of Γ-Al2o3 Nanoparticles in Flowing Ammonia

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Field Emission of Aluminum Nitride Nanocones Deposited on Titanium Substrate

Synthesis of AlN particles via direct nitridation in a drop tube furnace

Synthesis of Aluminium Nitride by Direct Nitridation of Molten Al-Mg-Si Alloys

Growth of Spontaneous Nucleation AlN Crystals by Al-Base Alloy Evaporation in Nitrogen Atmosphere