Abstract:Abstract Spherical AlN powders with micrometer size have attracted great attention owing to their good fluidity and dispersity. However, the industrial preparation methods usually require high temperature and long soaking time, which lead to the high cost and limit the wide application of the products. Herein, nearly spherical AlN particles with the average size of 2.5 μm were successfully synthesized via an in-situ combustion synthesis method. The effect of N 2 pressure, NH 4 Cl content, and Al particle size on the combustion reaction procedure, phase composition, and microstructure of the products was systematically investigated. The results showed that the decreased N 2 pressure, increased NH 4 Cl content, and Al particle size led to the decreasing of combustion temperature and speed, which further affected the morphology of the products. As a result, low N 2 pressure (0.2 MPa), a small amount of NH 4 Cl (0.5 wt%), and fine Al particles (∼2.5 μm) contributed to a moderate combustion temperature and facilitated the formation of nearly spherical AlN particles. In addition, based on the gas-releasing assisted quenching experiments and thermo-kinetic analysis, a two-step growth mechanism for the nearly spherical AlN particles was rationally proposed. The present method shows the advantages of low cost and high efficiency for preparing nearly spherical AlN particles, which can be used as raw materials for electronic substrates and fillers for packaging materials.

In-Situ Chloride-Generated Route to Different AlN Nanostructures on Si Substrate

Evolution of Aluminum Nitride Nanostructures from Nanoflower to Thin Film on Silicon Substrate by Direct Nitridation of Aluminum Precursor

An In-Situ Chloride-Generated Route to Various One-Dimensional Nanostructures of Chromium-Based Compounds

Vertically aligned one-dimensional AlN nanostructures on conductive substrates: Synthesis and field emission

Improving the structural performance of low-temperature sputtered AlN on silicon substrate

Facile synthesis of monodisperse aluminum nitride microspheres

A Simple Route to Aligned AlN Nanowires

Preparation of single crystalline AlN thin films on ZnO nanostructures by atomic layer deposition at low temperature

One-step Synthesis Route of the Aligned and Non-Aligned Single Crystalline Α-Si3n4 Nanowires

A general low-temperature CVD synthetic route to fabricate low-melting-point-metal compounds 1D nanostructures

Preparation and Characterization of AlN-Based Hierarchical Nanostructures with Improved Chemical Stability

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Controllable Synthesis of One-Dimensional Aluminum Nitride Nanostructures Through Vapor-Solid Epitaxial Growth

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

6-Fold-symmetrical aln hierarchical nanostructures: Synthesis and field-emission properties

High Quality AlN Film Grown on a Nano-Concave-circle Patterned Si Substrate with an AlN Seed Layer

Sublimation Growth of Aluminum Nitride on Silicon Carbide Substrate with Aluminum Nitride–silicon Carbide Alloy Transition Layer

Synthesis and Characterization of Several alpha-Silicon Nitride Nanostructures

Morphology Evolution, Growth Mechanism and Optical Properties of AlN Nanostructures

Toward homogenous AlN via reaction of Al nanoparticles with N 2 and NH 3 : Reactive molecular dynamics simulation

0001] oriented aluminum nitride one-dimensional nanostructures: synthesis, structure evolution, and electrical properties