Abstract:Nanowires have a wide range of applications, such as transparent electrodes, Li-ion battery anodes, light-emitting diodes, solar cells, and electronic devices. Currently, aluminum (Al) nanowires can be synthesized by thermally induced substitution of germanium (Ge) nanowires, chemical vapor deposition on other metal substrates, and template-assisted growth methods. However, there are still challenges in fabricating extremely high-purity nanowires, large-scale manufacturing, and simplifying the synthesis process and conditions. Here, we report for the first time that single-crystal Al nanowires can be one-step, in situ synthesized on a reduced graphene oxide (RGO) substrate on a large scale without using any catalysts. Through a simple high temperature treatment process, commercial micro-sized Al powders in RGO film were transformed into a single-crystal Al nanowire with an average length of 1.2 μm and an average diameter of 18 nm. The possible formation mechanism of the single-crystal Al nanowires is proposed as follows: hot aluminum atoms eject from the pristine aluminum/alumina core/shell structure of Al powders when they build up enough energy from the thermal stress under high temperature and confined space conditions, which is supported by both experimental and computational results. The method introduced here can be extended to allow the synthesis of one-dimensional highly reactive materials, like alkali metal nanowires, in confined spaces.

One-step Synthesis Route of the Aligned and Non-Aligned Single Crystalline Α-Si3n4 Nanowires

Ultrafast growth of single-crystalline Si nanowires

Ordered Arrays of High-Quality Single-Crystalline Α-Si3n4 Nanowires: Synthesis, Properties and Applications

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Controlled-Direction Growth of Planar InAsSb Nanowires on Si Substrates Without Foreign Catalysts

One-Step, Catalyst-Free, Scalable in Situ Synthesis of Single-Crystal Aluminum Nanowires in Confined Graphene Space

Array-orderly single crystalline silicon nano-wires

Synthesis and photoluminescence of aligned straight silica nanowires on Si substrate

Crystallization and Raman Shift of Array-Orderly Silicon Nanowires after Annealing at High Temperature

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

Silicon nano-wires grown at low temperature

Ultra‐Long Single‐Crystalline Α‐si3n4nanowires: Derived from a Polymeric Precursor

Synthesis of Single-Crystalline Α-Si3n4nanobelts by Extended Vapour–liquid–solid Growth

A New Route to Large‐Scale Synthesis of Silicon Nanowires in Ultrahigh Vacuum

Mass Production of Α-Silicon Nitride Single-crystalline Nanowires

Silicon Nano-Wires Fabricated by a Novel Thermal Evaporation of Zinc Sulfide

Large-scale synthesis of Si 3 N 4 nanowires by a modified carbothermal reduction method using graphite felt as growth substrate

Low-temperature Growth and Raman Scattering Study of Vertically Aligned ZnO Nanowires on Si Substrate

A Simple Route to Aligned AlN Nanowires

Synthesis and Characterization of Single-Crystalline Alumina Nanowires

Epitaxial Growth of Vertically Free-Standing Ultra-Thin Silicon Nanowires.