Abstract:Rare-earth-doped SiAlON and Si3N4 materials from aluminosilicate starting materials have been reported to show superior photoluminescence (PL) properties. Three different starting materials, including pulverized coal furnace fly ash, diatomite and raw illite, were used for synthesis of nitride materials. The phase and morphology evolution of these products were carefully monitored at the low temperature range of 1350 °C to 1450 °C by X-ray diffraction (XRD), scanning electronic microscopy (SEM) and Fourier-transform infrared spectroscopy (FT-IR). The PL properties of Eu-doped nitride products were also comparatively characterized. The results show that the type of starting material affects the phase composition and the photoluminescence properties of products. The existence of aluminum and alkali metals could effectively promote nitridation reactions. Aluminum in the starting materials led to the formation of different aluminum-rich nitride phases. Thus, β-SiAlON could be achieved at a much lower temperature (1350 °C) using raw illite or fly ash containing the proper amount of aluminum. Additionally, excess aluminum led to the formation of corundum and 15R-SiAlON. The products from pulverized coal furnace fly ash had more prismatic particles, and the products from diatomite had more fibrous particles. With the progress of the nitridation process, the fibers were increased, becoming longer and straighter, and the prismatic particles were more obvious. The presence of aluminum in the starting materials led to a blue shift in the photoluminescence spectrum.

Synthesis of Ultrafine AlN Powders in an Al-OC-N System

Preparation of AlN Powder of Low Oxygen Content Via Carbothermal Reduction and Nitridation by Active Gas Exchange Technique

Synthesis of Ultrafine AlN Powders in an Al-O-C-N System

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

AlN Powder Synthesis by Sodium Fluoride-Assisted Carbothermal Combustion

Facile synthesis of monodisperse aluminum nitride microspheres

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Synthesis of AlN nanocrystalline powders

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

SYNTHESIS OF ALUMINUM NITRIDE POWDER BY IN SITU REACTION

Effects of Al2o3 Phase Composition on Alon Powder Synthesis Via Aluminothermic Reduction and Nitridation

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Synthesis of Nanocrystalline Aluminum Nitride by Nitridation of Δ‐al2o3 Nanoparticles in Flowing Ammonia

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Efficient and cost-effective method to synthesize highly purified Ti<sub>4</sub>AlN<sub>3</sub> and Ti<sub>2</sub>AlN

AlN ceramics synthesized by carbothermal reduction of mechanical activated Al2O3

Thermodynamic and kinetic analyses of vacuum synthesis of AlN by the alumina carbothermal reduction nitridation method

Carbothermal Reduction Nitridation of Fly Ash, Diatomite and Raw Illite: Formation of Nitride Powders with Different Morphology and Photoluminescence Properties

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Combustion synthesis of fine aluminum nitride powders under micropositive N 2 pressure with water additive