Abstract:Abstract Spherical AlN powders with micrometer size have attracted great attention owing to their good fluidity and dispersity. However, the industrial preparation methods usually require high temperature and long soaking time, which lead to the high cost and limit the wide application of the products. Herein, nearly spherical AlN particles with the average size of 2.5 μm were successfully synthesized via an in-situ combustion synthesis method. The effect of N 2 pressure, NH 4 Cl content, and Al particle size on the combustion reaction procedure, phase composition, and microstructure of the products was systematically investigated. The results showed that the decreased N 2 pressure, increased NH 4 Cl content, and Al particle size led to the decreasing of combustion temperature and speed, which further affected the morphology of the products. As a result, low N 2 pressure (0.2 MPa), a small amount of NH 4 Cl (0.5 wt%), and fine Al particles (∼2.5 μm) contributed to a moderate combustion temperature and facilitated the formation of nearly spherical AlN particles. In addition, based on the gas-releasing assisted quenching experiments and thermo-kinetic analysis, a two-step growth mechanism for the nearly spherical AlN particles was rationally proposed. The present method shows the advantages of low cost and high efficiency for preparing nearly spherical AlN particles, which can be used as raw materials for electronic substrates and fillers for packaging materials.

Preparation of Spherical AlN Granules Directly by Carbothermal Reduction–Nitridation Method

Carbothermal Synthesis of Spherical AlN Granules: Effects of Synthesis Parameters and Y2O3 Additive

Carbothermal Synthesis of Micro-Scale Spherical Aln Granules with Caf2 Additive

Facile synthesis of monodisperse aluminum nitride microspheres

Carbothermal Synthesis of Spherical AlN Fillers

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Impact of Various Input Parameters on the Preparation of Different AlN Nanostructures by Hybrid Route of Hydrothermal and Carbothermal Reduction Nitridation Technique

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Preparation of Aluminum Nitride Granules by Aqueous Colloidal Process and the Characteristics of the Sintered Body

Preparation of AlN Powder of Low Oxygen Content Via Carbothermal Reduction and Nitridation by Active Gas Exchange Technique

Synthesis of Ultrafine AlN Powders in an Al-OC-N System

Synthesis of Aluminum Nitride by Nitridation of Γ-Al2o3 Nanoparticles in Flowing Ammonia

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Synthesis of Aluminium Nitride by Direct Nitridation of Molten Al-Mg-Si Alloys

Hydrolysis control of AlN powders for the aqueous processing of spherical AlN granules

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis of Nanocrystalline Aluminum Nitride by Nitridation of Δ‐al2o3 Nanoparticles in Flowing Ammonia