Magnetotransport, spin reorientation, and anomalous ferrimagnetic-to-antiferromagnetic phase transition in epitaxial Mn 2 Sb alloy thin films
Ting-Wei Chen,Shiqi Liu,Ying Zhang,Fang Tang,Jing-Shi Ying,Shuang-Shuang Li,Lei Chen,Fu-Sheng Luo,Shu-Juan Zhang,Yong Fang,Shanming Ke,Weiyao Zhao,Ren-Kui Zheng
DOI: https://doi.org/10.1016/j.actamat.2023.119257
IF: 9.4
2023-08-21
Acta Materialia
Abstract:High-quality ferrimagnetic Mn 2 Sb epitaxial thin films have been successfully grown on SrTiO 3 (001) single-crystal substrates via systematically optimizing the growth parameters using molecular beam epitaxy. Magnetotransport and magnetic measurements reveal that a spin reorientation transition occurs in the 260-150 K region where the direction of spins rotates from out-of-plane to in-plane upon cooling, resulting in the ferrimagnetic(II) phase, followed by a giant magnetoresistance associated anomalous ferrimagnetic(II)-to-canted antiferromagnetic ( c -AFM) phase transition in the 150-115 K region, resulting in the c -AFM ground state, both of which are completely absent and have yet not been observed in Mn 2 Sb bulk and thin films as of now. Temperature-dependent X-ray diffraction measurements reveal that the low-temperature c -AFM phase originates from the contraction of the out-of-plane lattice constant c , which would increase the exchange interaction between Mn(I) and Mn(II) atoms and thus stabilize the c -AFM phase. For the 24-nm films, there is almost no out-of-plane magnetization in the ground state, but exists a weak in-plane remanent magnetization (∼0.4 μ B/f.u.) and anomalous Hall effects, implying spin canting within the ab plane. With decreasing film thickness from 64 to 8 nm, the out-of-plane saturation magnetization at 10 K increases by approximately 10 times, and for the 8-nm film, its saturation magnetization (4.8 μ B/f.u.) is 2.8 times larger than that of Mn 2 Sb bulk (∼1.74 μ B/f.u.), both of which are attributed to the interfacial strain effect. Our work demonstrates that Mn 2 Sb films grown on perovskite oxide substrates show anomalous spin-charge-lattice coupling phenomena, which may inspire more study of its basic properties and potential device applications.
materials science, multidisciplinary,metallurgy & metallurgical engineering